Lithium Storage Properties of Hierarchical MoS2/C Composite Materials
Yang Zichuan, Xiang Jianan, Wang Xiaxia, Tian Jianhua, Shan Zhongqiang
School of Chemical Engineering and Technology, Tianjin University, Tianjin 300350, China

Abstract
Reference
Related Articles
Download: PDF (15933KB)   HTML ()   Export: BibTeX or EndNote (RIS)      Supporting Info
Guide  
Abstract Flower-like MoS2/C composite materials were prepared by one-pot ethanol/water composite solvothermal and postsintering method using MoS2 and glucose as raw materials. The reasonable composition of the ethanol/water composite solvent and the reasonable carbon content in the MoS2/C composite material were investigated. The morphology of MoS2/C samples were characterized using SEM and TEM. The carbon content of MoS2/C materials was tested and calculated using TGA. The electrochemical properties of the MoS2/C electrodes were investigated by cyclic voltammetry, galvanostatic charge-discharge measurements and electrochemical impedance spectroscopy. The result indicated that MoS2/C composite materials exhibits hierarchical flower-like structure, which eases the agglomeration of MoS2 and increases the utilization and electrochemical stability of the electrode active materials. When VethanolVwater=1:2 and the carbon content is 50%,the MoS2/C electrode delivers a reversible capacity of 762 mA·h·g-1 at a current density of 200 mA·g-1 after 100 cycles.
Service
Email this article
Add to my bookshelf
Add to citation manager
Email Alert
RSS
Articles by authors
Yang Zichuan
Xiang Jianan
Wang Xiaxia
Tian Jianhua
Shan Zhongqiang
Keywordslithium ion batteries;   negative electrode materials;   molybdenum disulfide;   hierarchical;   glucose     
Received 2020-08-06;
Fund
About author:
Cite this article:   
Yang Zichuan, Xiang Jianan, Wang Xiaxia, Tian Jianhua, Shan Zhongqiang.Lithium Storage Properties of Hierarchical MoS2/C Composite Materials[J]  Chemcial Industry and Engineering, 2021,V38(3): 70-77
Copyright 2010 by Chemcial Industry and Engineering