CsX分子筛催化丙酮制备异佛尔酮

摘要采用离子交换法和浸渍法向NaX分子筛引入Cs进行改性，分别记做CsX-IE和CsX-IMP。采用SEM、XRD、FT-IR、BET、TG和CO₂-TPD等分析手段对催化剂进行表征，并在固定床微反应器装置上，对改性后的分子筛催化丙酮缩合制备异佛尔酮反应进行了催化性能评价。研究表明：2种制备方法得到的改性后分子筛催化剂均具有完整的晶体结构、较大的比表面积、适当的碱性位和良好的热稳定性，催化活性比较高。同时得到适宜的工艺条件：反应温度350℃，液时空速2.0 h^-1，在此工艺条件下，丙酮的转化率为26.05%，异佛尔酮的选择性为52.27%。

	Service

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	马莉
	姜斌
	任海伦

关键词：异佛尔酮 CsX分子筛离子交换法浸渍法

Abstract： The modified X molecular sieves were prepared by the ion-exchange method and the impregnation method, named as CsX-IE and CsX-IMP respectively. The characterization of CsX-IE and CsX-IMP were carried out by the use of SEM, XRD, FT-IR, BET, TG and CO₂-TPD techniques. The catalytic performance, including the catalytic activity, selectivity and stability, were evaluated in the reaction of the acetone vapor-solid phase condensation using a micro fixed-bed reactor. Characterization results show that CsX-IE and CsX-IMP molecular sieves catalysts both have the complete crystal structure, large surface area, the proper basic site and good thermal stability. The conditions on preparation of isophorone by condensation of acetone via modified molecular sieves catalysts were studied. The results show that the optimum reaction temperature is 350℃, and the best LHSV of acetone is 2.0 h^-1. Under this conditions, the acetone conversion rate can reach 26.05%, the selectivity of isophorone is 52.27%.

Keywords： isophorone； CsX molecular sieve； ion-exchange method； impregnation method

Received 2016-05-24;

Corresponding Authors: 任海伦,E-mail:hlren@tju.edu.cn。 Email: hlren@tju.edu.cn

About author: 马莉(1990-),女,硕士研究生,现从事工业催化方面的研究。

引用本文:

马莉, 姜斌, 任海伦.CsX分子筛催化丙酮制备异佛尔酮[J]. 化学工业与工程, 2018,35(5): 12-18

Ma Li, Jiang Bin, Ren Hailun.Synthesis of Isophorone from Acetone over CsX Molecular Sieves[J]. Chemcial Industry and Engineering, 2018,35(5): 12-18

[1] 吕咏梅. 异佛尔酮合成技术进展与应用开发[J]. 化学推进剂与高分子材料, 2005, 35(2):20-22 Lü Yongmei. Synthetic technology progress and application development of isophorone[J]. Chemical Propellants & Polymeric Materials, 2005, 35(2):20-22(in Chinese)
[2] 谢丽莎, 陈霄榕. 固体酸碱性质对丙酮缩合生成异佛尔酮反应的影响[J]. 化工进展, 2010, 29(7):1230-1234 Xie Lisha, Chen Xiaorong. Effect of solid base properties on acetone condensation to isophorone over Mg-Al-O catalyst[J]. Chemical Industry and Engineering Progress, 2010, 29(7):1230-1234(in Chinese)
[3] 苑丽质. 催化剂制备方法对丙酮气相合成异佛尔酮的影响[J]. 化学世界, 2015, 56(3):136-139 Yuan Lizhi. Effect of catalyst preparation methods on sy-nthesis of isophorone from vapour phase acetone[J]. Chemical World, 2015, 56(3):136-139(in Chinese)
[4] 马春香, 刘钢, 朱万春, 等. 共沉淀法制备的镁铝氧化物催化剂上丙酮气相缩合反应[J]. 高等学校化学学报, 2009, 30(12):2429-2433 Ma Chunxiang, Liu Gang, Zhu Wanchun, et al. Gas-Phase aldol condensation of acetone over Mg-Al oxides prepared by co-precipitation methods[J]. Chemical Journal of Chinese Universities, 2009(12):2429-2433(in Chinese)
[5] 王玉环, 王国甲, 肖军华, 等. 丙酮在固体碱催化剂上的缩合反应[J]. 高等学校化学学报, 1993, (10):1448-1450 Wang Yuhuan, Wang Guojia, Xiao Junhua, et al. The condensation of acetone over solid base catalyst[J]. Chemical Journal of Chinese Universities, 1993, (10):1448-1450(in Chinese)
[6] Cosimo J I D, DiEz V K, Apestegui A C R. Synthesis of α,β-unsaturated ketones over thermally activated Mg-Al hydrotalcites[J]. Applied Clay Science, 1998, 13(5/6):433-449
[7] Kelkar C P, Schutz A A. Efficient hydrotalcite-based catalyst for acetone condensation to α-isophorone-Scale up aspects and process development[J]. Applied Clay Science, 1998, 13(5/6):417-432
[8] 王芳珠, 杨坤, 柴永明, 等. 以镁铝水滑石为前驱体制备复合氧化物催化丙酮气相缩合反应[J]. 无机化学学报, 2008, 24(9):1417-1423 Wang Fangzhu, Yang Kun, Chai Yongming, et al. Acetone gas phase condensation on Mg-Al composite oxides catalysts prepared via Mg-Al hydrotalcites precursor[J]. Chinese Journal of Inorganic Chemistry, 2008, 24(9):1417-1423(in Chinese)
[9] Zamora M, López T, Gómez R, et al. Oligomerization of acetone over titania-doped catalysts (Li, Na, K and Cs):Effect of the alkaline metal in activity and selectivity[J]. Catalysis Today, 1999, 23(11):1101-1119
[10] Zamora M, López T, Gómez R, et al. Acetone gas phase condensation on alkaline metals doped TiO₂ sol-gel catalysts[J]. Applied Surface Science, 2005, 252(3):828-832
[11] 郑平, 阮济之. 丙酮在沸石催化剂上的缩合反应[J]. 精细化工, 1993, (1):32-35 Zheng Ping, Ruan Jizhi. Study of acetone condensation on zeolite catalysts[J]. Fine Chemicals, 1993, (1):32-35(in Chinese).
[12] Fukada I, Matsuba K. Preparation of dehydrated condensates of acetone with zeolite catalysts:JP, 9059204 A[P].1997-12-24
[13] Stevens M G, Chen D, Foley H C. Oxidized caesium/nanoporous carbon materials:Solid-Base catalysts with highly-dispersed active sites[J]. Chemical Communications, 1999, 3(3):275-276
[14] Flego C, Perego C. Acetone condensation as a model reaction for the catalytic behavior of acidic molecular sieves:A UV-Vis study[J]. Applied Catalysis A-General, 2000, 192(192):317-329
[15] Salvapati G S, Ramanamurty K V, Janardanarao M. Selective catalytic self-condensation of acetone[J]. Journal of Molecular Catalysis, 1989, 54(1):9-30
[16] Reichle W T. Pulse microreactor examination of the vapor-phase aldol condensation of acetone[J]. Journal of Catalysis, 1980, 63(2):295-306
[17] Tsou J, Magnoux P, Guisnet M, et al. Catalytic oxidation of methyl-isobutyl-ketone over basic zeolites[J]. Applied Catalysis B Environmental, 2004, 51(2):129-133
[18] Kovacheva P, Arishtirova K, Davidova N. Effect of preparation of a CsX zeolite catalyst on the oxidative conversion of methane[J]. Applied Catalysis A General, 1997, 163(1):255-260
[19] Krauze A, Duburs G. Effect of preparation of a CsX zeolite catalyst on the oxidative methylation of toluene with methane[J]. Applied Catalysis A General, 1998, 167(2):271-276
[20] Romero M D, Ovejero G, Rodríguez A, et al. Impregnation of X zeolite with alkaline hydroxide during the synthesis[J]. Journal of Porous Materials, 2003, 11(1):31-39