Chemcial Industry and Engineering 2004, Vol. 21 Issue (2) :84-86    DOI:
Article Current Issue | Next Issue | Archive | Adv Search << | >>
The Synthesis of MnFe_2O_4 Nanocrystals and Their Characterization
WANG Xiu-yu,YANG Gui-qin,YAN Le-mei,MENG Jian-hua,SUN Yi-huan(School of Sciences,Tianjin University,Tianjin 300072,China)
(School of Sciences,Tianjin University,Tianjin 300072,China

Abstract
Reference
Related Articles
Download: PDF (0KB)   HTML ()   Export: BibTeX or EndNote (RIS)      Supporting Info
Abstract MnFe_2O_4 nanocrystals were prepared by low-temperature coprecipitation method,high temperature method and hydrothermal method respectively.And the samples obtained by the three methods were characterized by XRD,TEM and VSM.The preparation for MnFe_2O_4 nanocrystals using precursor with low-temperature coprecipitation method was studied in detail.Comparison and analysis of the three methods indicated that low-temperature coprecipitation method was optimal in the preparation of pure samples with small size.
Service
Email this article
Add to my bookshelf
Add to citation manager
Email Alert
RSS
Articles by authors
Keywords:   
Received 2004-03-15; published 2004-03-15
Cite this article:   
WANG Xiu-yu,YANG Gui-qin,YAN Le-mei,MENG Jian-hua,SUN Yi-huan.The Synthesis of MnFe_2O_4 Nanocrystals and Their Characterization[J]  Chemcial Industry and Engineering, 2004,V21(2): 84-86
Copyright 2010 by Chemcial Industry and Engineering