Synthesis and Characterization of Epoxy Resin Modified with Polyurethane
CHANG Li,LIU Wei,YAO Fang-lian(School of Chemical Engineering and Technology,Tianjin University,Tianjin 300072,China)
(School of Chemical Engineering and Technology,Tianjin University,Tianjin 300072,China

Abstract
Reference
Related Articles
Download: PDF (283KB)   HTML 1KB   Export: BibTeX or EndNote (RIS)      Supporting Info
Abstract Di-functional(PU-B) and tri-functional(PU-A and PU-D) polyurethane prepolymers were prepared from toluene diisocyanate(TDI) and polyether polyhydric alcohol(N-330 and PF-15).Through the graft reaction of the obtained polyurethane prepolymers with epoxy resins,and then cross-linking with dicyamine,a series of epoxy resins modified with polyurethane were synthesized.The effects of structures and dosages of epoxy resins and polyurethane prepolymers,as well as the dosages of thickening agent silica derivates on the adhesive properties of EPR-PU composite system were investigated in detail.The results indicated that the optimum composition of EPR-PU system is m(E-51)��m(E-20)��m(PU-D)��m(PU-A)=3��2��0.06��0.54,at which the mechanical strengths of the adhesive reach the highest level.
Service
Email this article
Add to my bookshelf
Add to citation manager
Email Alert
RSS
Articles by authors
Keywords��   
Received 2008-11-15; published 2008-11-15
Cite this article:   
CHANG Li,LIU Wei,YAO Fang-lian.Synthesis and Characterization of Epoxy Resin Modified with Polyurethane[J]  Chemcial Industry and Engineering, 2008,V25(6): 499-502
Copyright 2010 by Chemcial Industry and Engineering