Fabrication of Organic-Inorganic Composite Adhesives Used for Refractories
DUAN Hui,ZHENG Hua,ZHU Xiao-jin(College of Materials Science and Metallurgical Engineering,Wuhan University of Science and Technology,Wuhan 430081,Hubei Province,China)
(College of Materials Science and Metallurgical Engineering,Wuhan University of Science and Technology,Wuhan 430081,Hubei Province,China

Abstract
Reference
Related Articles
Download: PDF (181KB)   HTML ()   Export: BibTeX or EndNote (RIS)      Supporting Info
Abstract Because CaO contained in the cement castable can generate the low total melting,the properties of cement castables at high temperature can be weakened.Therefore,we need to develop a new binder to replace cement to improve the properties at high temperature,as well as at room temperature.Based on acrylamide gel system a new type of binder for castables was developed by adding micropowder.It was concluded that after drying at(110 ℃,) the castable showed good properties such as the bulk density,apparent porosity,cold crushing strength and bending strength,especially bending strength was improved largely.Through sintering at high temperature,better properties of the castable was obtained.
Service
Email this article
Add to my bookshelf
Add to citation manager
Email Alert
RSS
Articles by authors
Keywords：   
Received 2009-09-15; published 2009-09-15
Cite this article:   
DUAN Hui,ZHENG Hua,ZHU Xiao-jin.Fabrication of Organic-Inorganic Composite Adhesives Used for Refractories[J]  Chemcial Industry and Engineering, 2009,V26(5): 400-403
Copyright 2010 by Chemcial Industry and Engineering