Chemcial Industry and Engineering 2010, Vol. 27 Issue (3) :233-236    DOI:
Article Current Issue | Next Issue | Archive | Adv Search << | >>
Anti-Corrosion Properties of Polyaniline Coating on X70 Steel
SU Dan-dan,YANG Xiao-xia,JIA Qing-ming (Faculty of Chemical Engineering,Kunming University of Science and Technology,Kunming 650224,China)
(Faculty of Chemical Engineering,Kunming University of Science and Technology,Kunming 650224,China

Abstract
Reference
Related Articles
Download: PDF (165KB)   HTML 1KB   Export: BibTeX or EndNote (RIS)      Supporting Info
Abstract In this paper,the anticorrosion properties of polyaniline coating on X70 steel in acid (5% HNO3 ),weak alkaline (saturated Na2CO3),alkaline (5% KOH) solution were studied by using polarization and AC impedance technique. The results showed that polyaniline coat had an obvious anticorrosive effect on X70 steel in all these three kinds of solutions,and in a short period of time,polyaniline in acidic solution showed the best anticorrosive properties. In addition,saturated Na2CO3 solution was used to simulate the soil environment,so that we could study the changing discipline of X70 steel electrode covered with polyaniline film. Polarization and AC impedance analysis showed that polyaniline had perdurable anticorrosive properties to X70 steel,and its anticorrosive mechanism should be polyaniline's shielding and protective effect on the anode (passive role).
Service
Email this article
Add to my bookshelf
Add to citation manager
Email Alert
RSS
Articles by authors
Keywords��   
Received 2010-05-15; published 2010-05-15
Cite this article:   
SU Dan-dan,YANG Xiao-xia,JIA Qing-ming .Anti-Corrosion Properties of Polyaniline Coating on X70 Steel[J]  Chemcial Industry and Engineering, 2010,V27(3): 233-236
Copyright 2010 by Chemcial Industry and Engineering