Facile Preparation of Hollow Mesoporous Silica Nanoparticles Coated with pH-Sensitive Polymer
Zhong Qing, Zhang Jianhua, Guo Ruiwei
School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China

Abstract
Reference
Related Articles
Download: PDF (1691KB)   HTML ()   Export: BibTeX or EndNote (RIS)      Supporting Info
Abstract 

Trimethoxysilyl-propyl-trithiocarbonyl-benzyl ester(BTPT), which is one of the silicone-based RAFT agents, was grafted onto the surface of silica nanospheres. Using the reversible addition-fragmentation chain transfer polymerization, silica nanospheres modified with the pH-and temperature-sensitive polyelectrolyte poly(N, N-dimethylaminoethyl methacrylate) (PDMAEMA) were prepared. Then silica nanospheres grafted with PDMAEMA were transformed to the hollow mesoporous structure by surface-protected etching strategy using ammonia at ambient temperature, thereby obtained the hollow mesoporous silica nanospheres modified with the PDMAEMA (HMS@PDMAEMA). The resultant composite nanoparticles with pH-and temperature-sensitive polymer shell and HMS core were characterized by a variety of techniques such as 1HNMR, FTIR, GPC and TEM, etc. The pH-sensitive behavior was tested by nano-size and zeta potential analyzer. We envision that the HMS@PDMAEMA should have potential applications in controlled release of anticancer drug and gene delivery.

Service
Email this article
Add to my bookshelf
Add to citation manager
Email Alert
RSS
Articles by authors
Zhong Qing
Zhang Jianhua
Guo Ruiwei
Keywordshollow mesoporous silica nanoparticles;   surface modification;   polymer;   pH-sensitive behavior     
Received 2015-04-21;
About author:
Cite this article:   
Zhong Qing, Zhang Jianhua, Guo Ruiwei.Facile Preparation of Hollow Mesoporous Silica Nanoparticles Coated with pH-Sensitive Polymer[J]  Chemcial Industry and Engineering, 2017,V34(2): 50-54
Copyright 2010 by Chemcial Industry and Engineering