PET-PTMG聚醚酯熔融与结晶行为的研究

摘要采用熔融缩聚法合成了一系列聚对苯二甲酸乙二醇酯(PET)-四氢呋喃聚醚(PTMG)聚醚酯,用DSC、偏光显微镜表征了材料的熔融与结晶性能,讨论了组成对聚醚酯的熔点、结晶温度、结晶度、结晶形态的影响。结果表明,PET-PTMG聚醚酯的熔点与组成的关系符合Baur公式;其结晶度随着聚醚含量的增加呈现先升高后下降的趋势;并为明显的结晶与非结晶的两相结构形态。

	Service

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	贾宏涛
	赵蕴慧
	盛京

关键词： PET-PTMG聚醚酯熔融行为结晶行为结晶形态

Abstract： Poly(ether-ester)s based on poly(ethylene terephthalate)poly(tetramethylene glycol) (PET-PTMG) were synthesized by melt polycondensation. The melting and crystallization behavior PET-PTMG poly(ether-ester) were measured by DSC and polarizing optical microscope. The effect of poly(ether-ester) composition on its melting temperature,crystallization temperature,crystalinity and crystal morphology was discussed. Results showed that the melting temperatures of poly(ether-ester) are well correlated to composition by Baur's equation. Poly(ether-ester) possess a two-phase morphology consisting of crystalline and amorphous regions.

Keywords：

Received 2003-11-15; published 2003-11-15

引用本文:

贾宏涛,赵蕴慧,盛京.PET-PTMG聚醚酯熔融与结晶行为的研究[J]. 化学工业与工程, 2003,20(6): 319-323

JIA Hong-tao,ZHAO Yun-hui,SHENG Jing.Study on Melting and Crystallization Behaviorof PET-PTMG Poly(ether-ester)[J]. Chemcial Industry and Engineering, 2003,20(6): 319-323

[1]	兰建武,吴大诚.聚醚酯嵌段共聚物熔体的流变性能[J].高分子学报,2000,(1):50-53.
[2]	GABRIELSEW,SOLIMANM,DIJKSTRAK.Microstructureandphasebehaviorofblockcopoly(etherester)thermoplasticelastomers[J].Macromolecules.2001,34:1685-1693
[3]	陈　稀,付波涛,王依民,等.聚酯-聚醚系列嵌段共聚物结晶性能的研究[J].中国纺织大学学报,1991,17(3):9-14.
[4]	MADZ,WANGMZ,ZHAOMC,etal.Crystallizationandmeltingbehaviorofthesoftandhardsegmentsinpoly(ester-ether)s[J].JournalofPolymerScience:PartB:PolymerPhysics,1999,37:2918-2927.
[5]	VILANOVAPC,RIBASSM.Isothermalcrystallizationofpoly(ethyleneterephrhalate)oflowmolecularweightbydifferentialscanningcalorimetry[J].Polymer.1985,26(3):423-428
[6]	FLORYPJ.Thermodynamicsofcrystallizationinhighpolymer[J].TheJournalofChemicalPhysics,1949,17(3):223-301.
[7]	VANKREVELENDW.Propertiesofpolymers[M].NewYork:Elsevier,1990.
[8]	LEESH,LIMSW,LEEKH.Propertiesofpotentiallybiodegradablecopolyesters[J].PolymerInternational,1999,48:861-867.
[9]	BAURVH.InfluenceofSequence-lengthdistributiononthemeltingendpointofcopolymer[J].MakromoleculesChemicals,1966,98:297-301.