氟化改性固体甲基铝氧烷负载茂金属催化剂的研究
邓修远1, 王立娟2, 姜涛1, 李健1
1. 天津科技大学化工与材料学院, 天津 300457;
2. 中国石油天然气股份有限公司石油化工研究院大庆化工研究中心, 黑龙江 大庆 163714
Study on fluorinated modified solid methylaluminoxane supported metallocene catalysts
DENG Xiuyuan1, WANG Lijuan2, JIANG Tao1, LI Jian1
1. College of Chemical Engineering and Materials Science, Tianjin University of Science & Technology, Tianjin 300457, China;
2. Daqing Chemical Research Center, Petrochemical Research Institute, China National Petroleum Corporation, Daqing 163714, Heilongjiang, China

摘要
参考文献
相关文章
Download: PDF (9094KB)   HTML ()   Export: BibTeX or EndNote (RIS)      Supporting Info
摘要 在茂金属催化剂聚合烯烃领域中,甲基铝氧烷(MAO)是常见的助催化剂,将甲基铝氧烷固化形成固体甲基铝氧烷(sMAO)可以起到助催化剂和载体的双重作用。以加入不同的氟代烷烃和氟代芳烃类化合物对sMAO进行改性。同时用双(1-丁基-3-甲基环戊二烯基)二氯化锆为茂金属活性组分负载到改性载体上,得到负载型茂金属催化剂,并用于乙烯淤浆聚合。使用十氟联苯、全氟己烷、1-氢全氟己烷作为改性剂,制备的改性催化剂的活性为1.58×106、1.42×106和1.46×106 g·mol-1,与改性前相比活性提升了17%~30%。
Service
把本文推荐给朋友
加入我的书架
加入引用管理器
Email Alert
RSS
作者相关文章
邓修远
王立娟
姜涛
李健
关键词茂金属催化剂   改性剂   氟代烷烃   淤浆聚合   甲基铝氧烷     
Abstract: In the field of metallocene catalyst polymerization of olefins, methylaluminoxane (MAO) is a common cocatalyst. Curing methylaluminoxane to form solid methylaluminoxane (sMAO) can play a dual role as a cocatalyst and carrier. In this study, sMAO is modified by adding different fluoroalkanes and fluoroaromatic compounds. Simultaneously, bis (1-butyl-3-methylcyclopentadienyl) zirconium dichloride was loaded onto a modified carrier as the active component of the metallocene to obtain a supported metallocene catalyst, which was used for ethylene slurry polymerization. Among them, using decafluorobiphenyl, perfluorohexane, and 1-hydroperfluorohexane as modifiers, and the activity of the prepared modified catalyst was 1.58×106,1.42×106 and 1.46×106 g·mol-1, showing 17% to 30% increase in activity compared to that before modification.
Keywordsmetallocene catalyst   modifiers   fluoroalkanes   slurry polymerization   solid methylaluminoxane     
Received 2024-02-17;
Corresponding Authors: 李健,教授,lijian@tust.edu.cn。     Email: lijian@tust.edu.cn
About author: 邓修远(1998—),男,硕士研究生,现从事茂金属催化乙烯聚合方面的研究。