耐高温交联酸压裂液的研制及其性能评价

文章导读

摘要针对黏弹性表面活性剂(VES)转向酸使用成本高，耐温性差以及现有胶凝酸破胶不完全的问题，本研究首先通过水溶液聚合法合成稠化剂和有机锆交联剂，然后在质量分数为20%的盐酸水溶液(下同)中将稠化剂通过有机锆交联剂进行交联，得到耐高温交联酸基液，再根据压裂液性能要求添加高温缓蚀剂、助排剂、铁离子稳定剂和黏土稳定剂，研发了一种耐180 ℃高温的交联酸压裂液。采用高温高压流变仪、压裂液摩阻测试仪和表界面张力测定仪等对交联酸压裂液进行性能评价。结果表明，所制备的交联酸压裂液在180 ℃、170 s^-1条件下剪切120 min后，黏度仍可维持为73 mPa·s，加入0.15%过硫酸铵破胶后，黏度降为3.2 mPa·s，高温流变性和破胶性能良好。

	Service

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	蒋其辉
	杨向同
	龚福忠

关键词：压裂液；交联酸；稠化剂；耐高温性能

Abstract： In view of the problems of high cost, poor temperature resistance (less than 160 ℃) and incompletely broken of viscoelastic surfactant system(VES) and existing gelling acid, the thickener and organic zirconium crosslinking agent were synthesized by aqueous solution polymerization at first. In this paper, the thickener was then cross-linked by an organic zirconium crosslinker in a 20% HCl solution, a high temperature resistant crosslinking acid base solution was obtained. Based on this, according to the performance requirements of fracturing fluid, a kind of cross-linked acid fracturing fluid resistant to 180 ℃ was developed by adding high-temperature corrosion inhibitor, drainage aid, iron ion stabilizer and clay stabilizer. The high temperature and high pressure remoter, fracturing fluid friction tester and surface interfacial tension tester were used to evaluate the performance of cross-linked acid fracturing fluid. The results show that the viscosity of the cross-linked acid fracturing fluid can be maintained as 73 mPa·s after shearing at 180 ℃ and 170 s^-1 for 120 min. When 0.15% ammonium persulfate was added to break the glue, the viscosity decreased to 3.2 mPa·s, showing a good temperature resistance and glue breaking performance.

Keywords： fracturing fluid； crosslinked acid； thickener； high-temperature resistance

Received 2021-07-08;

Fund:中国石油集团工程技术研究院有限公司院级课题（CPET202020）

Corresponding Authors: 蒋其辉,高级工程师,E-mail:jiangqihuidri@cnpc.com.cn Email: jiangqihuidri@cnpc.com.cn

About author: 蒋其辉(1986-)，男，博士，现从事油气藏增产改造工作液及关键技术领域研究

引用本文:

蒋其辉, 杨向同, 龚福忠.耐高温交联酸压裂液的研制及其性能评价[J]. 化学工业与工程, 2022,39(1): 51-57

JIANG Qihui, YANG Xiangtong, GONG Fuzhong.Development and evaluation of high temperature resistant cross-linked acid fracturing fluid system[J]. Chemcial Industry and Engineering, 2022,39(1): 51-57

[1] LIU Jiankun, JIANG Tingxue, WU Chunfang, et al. Alternate acid injection fracturing technology for tight sandstone reservoirs[J]. Special Oil & Gas Reservoirs, 2017, 24(5): 150-155(in Chinese) 刘建坤, 蒋廷学, 吴春方, 等. 致密砂岩交替注酸压裂工艺技术[J]. 特种油气藏, 2017, 24(5): 150-155
[2] SONG Qi, WANG Yanling, WANG Zhiming, et al. Study on high-temperature delayed cross-linked acid[J]. Natural Gas and Oil, 2015, 33(3): 67-70, 10(in Chinese) 宋奇, 王彦玲, 王志明, 等. 高温延迟交联型交联酸研究[J]. 天然气与石油, 2015, 33(3): 67-70, 10
[3] GONG Jincheng, WANG Yanling, LUO Mingliang, et al. Research and prospect of crosslinked acid fracturing fluid[J]. Applied Chemical Industry, 2020, 49(8): 2058-2062(in Chinese) 巩锦程, 王彦玲, 罗明良, 等. 交联酸压裂液体系研究进展及展望[J]. 应用化工, 2020, 49(8): 2058-2062
[4] LV Q, LI Z, LI B, et al. Study of nanoparticle-surfactant-stabilized foam as a fracturing fluid[J]. Industrial & Engineering Chemistry Research, 2015, 54(38): 9468-9477
[5] WANG Yonghui, LI Yongping, CHENG Xingsheng, et al. A new acid fracturing technique for carbonate reservoirs with high-temperature and deep layer[J]. Acta Petrolei Sinica, 2012, 33(S2): 166-173(in Chinese) 王永辉, 李永平, 程兴生, 等. 高温深层碳酸盐岩储层酸化压裂改造技术[J]. 石油学报, 2012, 33(S2): 166-173
[6] HE Shiyun. Optimization of a high temperature low corrosivity acid fluid for application at 180 ℃ high temperature[J]. Drilling Fluid & Completion Fluid, 2020, 37(2): 244-249(in Chinese) 何世云. 抗180 ℃高温低腐蚀酸液体系构建及应用[J]. 钻井液与完井液, 2020, 37(2): 244-249
[7] LI Dan, YI Xiangyi, WANG Yanlong, et al. Research situation of the new acid fracturing acid system applying to deep carbonate reservoir[J]. Petrochemical Industry Application, 2017, 36(7): 1-5(in Chinese) 李丹, 伊向艺, 王彦龙, 等. 深层碳酸盐岩储层新型酸压液体体系研究现状[J]. 石油化工应用, 2017, 36(7): 1-5
[8] SHI Xin, ZENG Wenguang, LIU Dongmei, et al. Preparation and corrosion inhibition of mannich base corrosion inhibitor with high temperature and high oxygen resistance[J]. Oilfield Chemistry, 2020, 37(3): 510-514, 521(in Chinese) 石鑫, 曾文广, 刘冬梅, 等. 抗高温高氧曼尼希碱缓蚀剂的制备与缓蚀性能[J]. 油田化学, 2020, 37(3): 510-514, 521
[9] MU Daifeng, JIA Wenfeng, YAO Yiming, et al. Study on the integration of gelled acid and crosslinked acid to form high temperature retarded acid[J]. Drilling Fluid & Completion Fluid, 2019, 36(5): 634-638(in Chinese) 穆代峰, 贾文峰, 姚奕明, 等. 胶凝酸与交联酸一体化耐高温缓速酸研究[J]. 钻井液与完井液, 2019, 36(5): 634-638
[10] LUO Zhao, LI Kehua, WU Xueqing, et al. Study of new corrosion inhibitor for retarded acid[J]. Advances in Fine Petrochemicals, 2006, 7(3): 7-9(in Chinese) 罗兆, 李克华, 吴学庆, 等. 缓速酸用缓蚀剂的研究[J]. 精细石油化工进展, 2006, 7(3): 7-9
[11] YOU F X. High temperature aqueous-based zirconium crosslinking composition and use: US20090114390[P]. 2009-05-07
[12] WANG Yizhi, KE Qiang, CHEN Qing, et al. Preparation and application of the diverting acid of water soluble inorganic salt particle[J]. Oil Drilling & Production Technology, 2018, 40(5): 641-646(in Chinese) 王艺之, 柯强, 陈清, 等. 水溶性无机盐颗粒转向酸的制备与应用[J]. 石油钻采工艺, 2018, 40(5): 641-646
[13] DAI Yating, YI Xiangyi, SUN Jun, et al. Review of acids for acid fracturing with proppant[J]. Petrochemical Industry Application, 2015, 34(3): 1-5, 10(in Chinese) 戴亚婷, 伊向艺, 孙骏, 等. 携砂酸液体系综述[J]. 石油化工应用, 2015, 34(3): 1-5, 10
[14] ZHAO Shijun, CHEN Zhongge, YI Xiangyi, et al. Acid corossion rock 3D laser scan instrument[J]. Instrument Technique and Sensor, 2010(7): 22-24(in Chinese) 赵仕俊, 陈忠革, 伊向艺, 等. 酸蚀岩板三维激光扫描仪[J]. 仪表技术与传感器, 2010(7): 22-24
[15] BALE A, SMITH M B, KLEIN H H. Stimulation of carbonates combining acid fracturing with proppant (CAPF): A revolutionary approach for enhancement of sustained fracture conductivity and effective fracture half-length[C]//Society of Petroleum Engineers. Florence, Italy: SPE, 2010
[16] SHI Yuyan, LIU Xiaoyan, ZHAO Wei, et al. Turnaround refracturing technology applied to change crack direction[J]. Offshore Oil, 2009, 29(2): 60-64(in Chinese) 时玉燕, 刘晓燕, 赵伟, 等. 裂缝暂堵转向重复压裂技术[J]. 海洋石油, 2009, 29(2): 60-64
[17] YAN Xu. Research on fiber temporary plugging and steering acidizing technology in low porosity and permeability carbonate reservoir[D]. Heilongjiang Daqing: Northeastern Petroleum University, 2017(in Chinese) 闫旭. 低孔渗碳酸盐岩储层纤维暂堵转向酸化技术研究[D]. 黑龙江大庆: 东北石油大学, 2017
[18] ZHENG Yunchuan, ZHAO Liqiang, LIU Pingli, et al. Application of amphoteric surfactants-based acid in matrix acidizing and acid fracturing[J]. Natural Gas Industry, 2005, 25(12): 71-73, 9(in Chinese) 郑云川, 赵立强, 刘平礼, 等. 两性表面活性剂酸液体系在基质酸化及酸压中的应用[J]. 天然气工业, 2005, 25(12): 71-73, 9
[19] WANG Xiaohong, LIU Youquan, LIAO Jun, et al. Study on the influence factor of diverting performance of self-diverting acid[J]. Chemical Engineering of Oil & Gas, 2012(2): 204-206, 249(in Chinese) 王小红, 刘友权, 廖军, 等. 转向酸转向性能影响因素研究[J]. 石油与天然气化工, 2012(2): 204-206, 249
[20] XIAO Bo, ZHANG Shicheng, ZHANG Xiong, et al. Optimization and evaluation of high temperature compatible sand crosslinking acid formulation[J]. Oilfield Chemistry, 2015, 32(1): 18-22(in Chinese) 肖博, 张士诚, 张雄, 等. 耐高温可携砂交联酸配方优化与评价[J]. 油田化学, 2015, 32(1): 18-22