硫酸改性核桃壳处理含Cr(Ⅵ)模拟废水研究

摘要在100 mL 8 mol·L^-1硫酸溶液中，核桃壳加入量为9 g，核桃壳颗粒度为100目，反应时间为3 h，反应温度为25 ℃的条件下制备得到硫酸改性核桃壳。硫酸改性核桃壳对Cr（Ⅵ）具有优异的吸附性能。详细探讨了硫酸改性核桃壳处理含Cr（Ⅵ）模拟废水的影响因素：废水pH值、Cr（Ⅵ）离子浓度、硫酸改性核桃壳用量、处理时间和处理温度等对Cr（Ⅵ）去除率的影响，并进一步通过正交试验及对比试验得出处理150 mL 200 mg·L^-1的含Cr（Ⅵ）模拟废水的最适宜处理工艺为：pH值为1，硫酸改性核桃壳用量为1.4 g，处理时间为2 h，处理温度为25 ℃，在此条件下，对Cr（Ⅵ）的去除率达到95.86%，Cr（Ⅵ）吸附量为20.54 mg·g^-1。

	Service

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	汤琪
	赵红静
	裴聪聪
	冷雪
	熊姚梦
	覃珊
	张瀚

关键词：硫酸改性核桃壳 Cr(Ⅵ) 处理工艺去除率

Abstract： Walnut shell modified by sulfuric acid was synthesized under the conditions that the volume of 8 mol·L^-1 sulfuric acid solution is 100 mL, walnut shell dosage is 9 g, particle size of walnut shell is 80 mesh, reaction time is 3 h, reaction temperature is 25 ℃. Walnut shell modified by sulfuric acid has excellent adsorption property to Cr(Ⅵ) ion. Some factors,such as the dosage of walnut shell modified by sulfuric acid, Cr(Ⅵ) ion concentration, pH, treatment time, treatment temperature which affect the removal rate of Cr(Ⅵ) ion, were investigated. The dispose technics were more optimized through orthogonal experiment and comparative experiment. When the volume of Cr(Ⅵ) ion simulated wastewater is 150 mL, Cr(Ⅵ) ion concentration is 200 mg·L^-1, the best dispose technics are as follows:pH=1, the dosage of walnut shell modified by sulfuric acid is 1.4 g, treatment time is 3 h, treatment temperature is 25 ℃. Under those conditions, the removal rate of Cr(Ⅵ) ion was 95.86% and the adsorption capacity of sorbent was 20.54 mg·g^-1.

Keywords： walnut shell modified by sulfuric acid； Cr(Ⅵ)； dispose technics； removal rate

Received 2020-10-19;

Fund:国家自然科学基金资助项目（21307168）；重庆市自然科学基金资助项目（cstcjjA50016）；重庆交通大学大创项目（X202010618076）。

Corresponding Authors: 汤琪,E-mail:83723885@qq.com。 Email: 83723885@qq.com

About author: 汤琪(1970-),男,副教授,博士,主要从事环境材料技术研究。

引用本文:

汤琪, 赵红静, 裴聪聪, 冷雪, 熊姚梦, 覃珊, 张瀚.硫酸改性核桃壳处理含Cr(Ⅵ)模拟废水研究[J]. 化学工业与工程, 2021,38(4): 73-77

Tang Qi, Zhao Hongjing, Pei Congcong, Leng Xue, Xiong Yaomeng, Qin Shan, Zhang Han.Treatment of Cr(Ⅵ) Ion in Simulated Wastewater by Walnut Shell Modified by Sulfuric Acid[J]. Chemcial Industry and Engineering, 2021,38(4): 73-77

[1] Wang J, Chen C. Biosorbents for heavy metals removal and their future[J]. Biotechnology Advances, 2009, 27(2):195-226
[2] Sud D, Mahajan G, Kaur M P. Agricultural waste material as potential adsorbent for sequestering heavy metal ions from aqueous solutions-A review[J]. Bioresource Technology, 2008, 99(14):6017-6027
[3] Sharma P K, Ayub S, Tripathi C N. Agro and horticultural wastes as low cost adsorbents for removal of heavy metals from wastewater:A review[J]. International Refereed Journal of Engineering and Science, 2013, 2(8):18-27
[4] Erta? R, Öztürk N. Removal of Cr(Ⅵ) from aqueous solution onto chestnut shell:Application of full factorial design and equilibrium studies[J]. Desalination and Water Treatment, 2013, 51(13/14/15):2909-2914
[5] Liu Z, Liu Y, Chen L, et al. Performance study of heavy metal ion adsorption onto microwave-activated banana peel[J]. Desalination and Water Treatment, 2014, 52(37/38/39):7117-7124
[6] Zafarani H R, Bahrololoom M E, Noubactep C, et al. Green walnut shell as a new material for removal of Cr(Ⅵ) ions from aqueous solutions[J]. Desalination and Water Treatment, 2015, 55(2):431-439
[7] Altun T, Pehlivan E. Removal of Cr(Ⅵ) from aqueous solutions by modified walnut shells[J]. Food Chemistry, 2012, 132(2):693-700
[8] 汤琪, 涂胜, 王孝华, 等. 苯胺改性核桃壳作为Pb(Ⅱ)吸附剂的改性工艺优化[J]. 化学工业与工程, 2019,36(5):36-42 Tang Qi, Tu Sheng, Wang Xiaohua, et al. Optimization of modification technics of aniline modified walnut shell as Pb(Ⅱ) adsorbent[J]. Chemical Industry and Engineering, 2019,36(5):36-42(in Chinese)
[9] 汤琪, 刘攀, 涂胜, 等. H₂O₂改性稻杆作为Pb²⁺吸附剂的工艺优化[J]. 化学工业与工程, 2020, 37(3):39-44, 59 Tang Qi, Liu Pan, Tu Sheng, et al. Technics optimization of hydrogen peroxide modified rice straw as Pb(Ⅱ) adsorbent[J]. Chemical Industry and Engineering, 2020, 37(3):39-44, 59(in Chinese)
[10] Singha B, Das S K. Biosorption of Cr(Ⅵ) ions from aqueous solutions:Kinetics, equilibrium, thermodynamics and desorption studies[J]. Colloids and Surfaces B:Biointerfaces, 2011, 84(1):221-232
[11] Bansal M, Garg U, Singh D, et al. Removal of Cr(Ⅵ) from aqueous solutions using pre-consumer processing agricultural waste:A case study of rice husk[J]. Journal of Hazardous Materials, 2009, 162(1):312-320
[12] Tyt?ak A, Oleszczuk P, Dobrowolski R. Sorption and desorption of Cr(Ⅵ) ions from water by biochars in different environmental conditions[J]. Environmental Science and Pollution Research, 2015, 22(8):5985-5994
[13] Garg U K, Kaur M P, Garg V K, et al. Removal of hexavalent chromium from aqueous solution by agricultural waste biomass[J]. Journal of Hazardous Materials, 2007, 140(1/2):60-68
[14] Liu H, Liang S, Gao J, et al. Enhancement of Cr(Ⅵ) removal by modifying activated carbon developed from Zizania caduciflora with tartaric acid during phosphoric acid activation[J]. Chemical Engineering Journal, 2014, 246:168-174
[15] Gupta V K, Pathania D, Sharma S, et al. Remediation of noxious chromium (Ⅵ) utilizing acrylic acid grafted lignocellulosic adsorbent[J]. Journal of Molecular Liquids, 2013, 177:343-352
[16] Vázquez G, Calvo M, Sonia Freire M, et al. Chestnut shell as heavy metal adsorbent:Optimization study of lead, copper and zinc cations removal[J]. Journal of Hazardous Materials, 2009, 172(2/3):1402-1414
[17] Zhu Y, Zheng Y, Wang F, et al. Fabrication of magnetic macroporous chitosan-g-poly (acrylic acid) hydrogel for removal of Cd²⁺ and Pb²⁺[J]. International Journal of Biological Macromolecules, 2016, 93:483-492