PLLA/PVA/PLCA三元共混体系分子间相互作用

摘要聚L-乳酸(PLLA)及聚乙烯醇(PVA)由于其良好的生物相容性,在生物医学领域得到了广泛的关注。但聚乳酸由于其疏水性及缺乏反应位点而使其应用受到一定的限制。将聚乙烯醇与聚乳酸共混,不仅可以降低聚乳酸的成本,同时可以改善其亲水性,但由于其结构差异,存在严重的相分离现象。本研究将含有反应活性位点的乳酸-柠檬酸共聚物(PLCA)引入PLLA/PVA体系中,以期改善二者的相容性。通过红外光谱分析手段,研究了PLLA/PVA/PLCA体系中分子间的相互作用,并对不同组成体系的力学性能进行了分析及表征。结果表明,PLCA的加入使PLLA/PVA复合体系的相容性及力学性能得到了明显的改善。

	Service

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	安晓燕
	张海玥
	白云
	陈炜
	常丽
	姚芳莲

关键词：聚乳酸聚乙烯醇共混红外光谱

Abstract： Poly(L-lactide)(PLLA) and poly(vinyl alcohol)(PVA) have been widely used as biomedical materials because of their good biocompatibility.However,clinical applications of PLLA have sometimes interfered with the high hydrophobic and lacking of reactive site.PVA is inexpensive compared with PLLA,and both hydrophilic and high flexible.Here the blends of PLLA/PVA/PLCA were prepared by solution casting.The copolymer of lactic acid and citric acid(PLCA) was added to improve the compatibility and hydrolysis rate of PLLA/PVA binary blends.The interactions between PLLA and PVA were investigated by FT-IR spectrum and the mechanical properties were also discussed.The results showed that compatibility of PLLA/PVA was improved and the mechanical strength was enhanced.

Keywords：

Received 2007-05-15; published 2007-05-15

引用本文:

安晓燕;张海玥;白云;陈炜;常丽;姚芳莲;.PLLA/PVA/PLCA三元共混体系分子间相互作用[J]. 化学工业与工程, 2007,24(3): 189-194

AN Xiao-yan,ZHANG Hai-yue,BAI Yun,CHEN Wei,CHANG Li,YAO Fang-lian.Molecular Interaction in PLLA/PVA/PLCA Blend System[J]. Chemcial Industry and Engineering, 2007,24(3): 189-194

[1]	YUDANOVA T N,SKOKOVA I F,ALESHINA E Y,et al.Polyvinyl alcohol film materials containing biopolymers:Preparation and properties[J].Fibre Chem,2000,32(50):347-352.
[2]	HEIDEMANN W,JESCHKEIT S,RUFFIEUX K,et al.Degradation of poly(D,L)lactide implants of calcium-phosphates with or without addition in vivo[J].Biomaterials,2001,22(17):2 371-2 381.
[3]	MIDDLETON J C,TIPTON A J.Synthetic biodegradablepolymers as orthopedic devices[J].Biomaterials,2000,21:2 335-2 346.
[4]	JEONG S I,KIM B S,KANG S W,et al.In vivobiocompatibility and degradation behavior of elastic poly(L-lactide-co-epsilon-caprolactone)scaffolds[J].Biomaterials,2004,25(28):5 939-5 946.
[5]	MATSUMURA G,HIBINO N,IKADA Y,et al.Successfulapplication of tissue engineered vascular autografts:Clinicalexperience[J].Biomaterials,2003,24(13):2 303-2 308.
[6]	IKEJIMA T,CAO A,YOSHIE N,et al.Surface compositionand biodegradability of poly(3-hydroxybutylic acid)/poly(vinyl alcohol)blend films[J].Polym Degrad Stab.1998,62:463-469
[7]	YOSHIE N,AZUMA Y,SAKURAI M,et al.Crystallizationand compatibility of poly(vinyl alcohol)/poly(3-hydroxybutyrate)blends:Influence of blend composition andtacticity of poly(vinyl alcohol)[J].J Appl Polym Sci.1995,56:17-24
[8]	IKEJIMA T,YOSHIE N,INOUE Y.Infrared analysis onblends of poly(3-hydroxybutyric acid)and steroregular poly(vinyl alcohol):Influence of tacticity of poly(vinyl alcohol)on crystallization of poly(3-hydroxybutyric acid)[J].Macromol Chem Phys.1996,197:869-880
[9]	KESEL C D,LEFEVERE C,NAGY J B,et al.Blends ofpolycaprolactone with polyvinyl alcohol:A DSC opticalmicroscopy and solid state NMR study[J].Polymer.1999,40:1-
[10]	TSUJI H,MURAMATSU H.Blends of aliphatic polyesters:VNon-enzymatic and enzymatic hydrolysis of blends fromhydrophobic poly(L-lactide)and hydrophilic poly(vinylalcohol)[J]..Polym Degrad Stab.2001,71:403-413
[11]	YAO Fang-lian,BAI Yun,CHEN Wei,et al.Synthesis andcharacterization of functionalL-lactic acid/citric acidoligomer[J].Eur Polymer J.2004,40:1-
[12]	YAO Fang-lian,BAI Yun,ZHOU Yu-tao,et al.Synthesisand characterization of multiblock copolymers based onL-lactic acid,citric acid and poly(ethylene glycol)[J].JPolym Sci:Part A:Polym Chem,2003,41:2 073.