陈化时间对磷酸三钙固体性能的影响

摘要研究了不同陈化时间下，磷酸三钙粒子的结晶度、形态特征以及粒度分布。采用X射线衍射仪测定了磷酸三钙的结晶度，用扫描电镜观测了磷酸三钙的外观形貌，并用马尔文粒度分析仪测定产物的粒度分布。实验表明：沉淀反应首先析出的是无定型沉淀物，陈化过程中发生晶化转变为晶型产品；无定型磷酸三钙转化为晶型磷酸三钙的过程中，通常伴随着溶液pH值的微微下降；SEM图可看出，产品最终形貌为片状聚集状态；随着陈化时间的增加，小颗粒逐渐溶解大颗粒逐渐长大，粒度分布变窄。

	Service

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	陈程
	党乐平
	卫宏远

关键词：磷酸三钙；陈化；结晶度；晶体形貌；粒度分布

Abstract： The effect of aging time on the solid performances of tricalcium phosphate was investigated by using XRD to identify the degree of crystallinity, and SEM to observe the crystal morphology. The Malvern particle size analyzer was also applied to measure the distribution of the particle size of tricalcium phosphate. It is found that the amourphous precipitation is initially produced, and then transforms to the crystal product during the aging process. The crystallization of calcium phosphates into crystalline tricalcium phosphate is accompanied with a slight decrease of the pH of the solution. According to the SEM image, the final morphology of the product is flake like aggregated crystals; with the increasing of aging time, small particles gradually dissolve, and larger particles gradually grow up, which leads to an arrow particle size distribution.

Keywords： tricalcium phosphate； aging time； degree of crystallinity； crystal morphology； particle size distribution

Received 2016-04-27;

Corresponding Authors: 党乐平,E-mail:dleping@163.com Email: dleping@163.com

About author: 陈程(1989-),女,硕士研究生,化学工程专业。

引用本文:

陈程, 党乐平, 卫宏远.陈化时间对磷酸三钙固体性能的影响[J]. 化学工业与工程, 2018,35(6): 62-66

Chen Cheng, Dang Leping, Wei Hongyuan.Influence of Aging Time on the Solid Performance of Tricalcium Phosphate[J]. Chemcial Industry and Engineering, 2018,35(6): 62-66

[1] 王静康. 工业结晶技术前沿[J]. 现代化工,1996, 10:19-22 Wang Jingkang. Industrial crystallization technology frontier[J]. Modern Chemical Industry, 1996, 10:19-22(in Chinese)
[2] 王静康. 工业结晶的现在与未来[J]. 化学工程,1992, 20(2):57-63 Wang Jingkang. The present and future of industrial crystallization[J]. Chemical Engineering, 1992, 20(2):57-63(in Chinese)
[3] 陈建峰,陈甘棠. 混合-反应结晶过程(I)实验[J]. 化学学报,1994, 45(2):176-182 Chen Jianfeng, Chen Gantang. Mixed-Reactive crystallization process (I) Experiment[J]. Acta Chimica Sinica, 1994, 45(2):176-182(in Chinese)
[4] Elliot J C. 18:Structure and chemistry of the apatites and other calcium orthophosphates (Studies in Inorganic Chemistry)[M]. New York:Elsevier Inc.,1994
[5] 王磊磊. 饲料级磷酸二氢钙、磷酸三钙和磷酸二氢钠的质量和安全特性研究[D]. 四川农业大学,2013 Wang Leilei. Study on the quality and safety characteristics of feed-grade calcium dihydrogen phosphate, tricalcium phosphate and sodium dihydrogen phosphate[D]. Sichuan Agricultural University, 2013(in Chinese)
[6] 张瑶,何岗,洪建和. 浅谈饲料级脱氟磷酸三钙的生产工艺研究[J]. 中国饲料,2012, 15:18-20 Zhang Yao, He Gang, Hong Jianhe. Study on production technology of feed grade defluorination tricalcium phosphate[J]. China Feed, 2012, 15:18-20(in Chinese)
[7] Wzorek Z, Kowalski Z. Calcium feed phosphate production using the low-temperature method[J]. Journal of Loss Prevention in the Process Industries, 2001, 14:365-369
[8] Posner A S, Betts F. Synthetic amorphous calcium phophate and its relation to bone mineral structure[J]. Accounts Chem Res, 1975, 8:273-281
[9] Tadic D, Peters F, Epple M. Continuous synthesis of amorphous carbonated apatite[J]. Biomaterials, 2002, 23:2553-2559
[10] Skrtic D, Antonucci J M, Eanes E D, et al. Silica and zirconia-hybridized amorphous calcium phosphate:Effect on transformation to hydroxyapatite[J]. J Biomed Mater Res, 2002, 59:597-604
[11] Bertoni E, Bigi A, Falini G, et al. Hydroxyapatite/polyac-rylic acid nanocrystals[J]. J Mater Chem, 1999, 9:779-782
[12] 宋云京,李木森,温树林. 人体密质骨的AFM观察分析[J]. 电子显微学报,2002, 21:695-696 Song Yunjing, Li Musen, Wen Shulin. The AFM observation and analysis of human cortical bone[J]. Journal of Chinese Electron Microscopy Society, 2002, 21:695-696(in Chinese)
[13] Nore P H, Mersmann A. Batch precipitation of barium carbonate[J]. Chem Eng Sci, 1993, 48(17):3083-3088