Chemcial Industry and Engineering 2002, Vol. 19 Issue (4) :297-300    DOI:
Article Current Issue | Next Issue | Archive | Adv Search << | >>
Synthesis and Properties of Skeleton Ti-Catalyst
ZENG Lei 1,FU Zai hui 2,YIN Du lin 2 (1.HuNan Environmental & Biologic College,HengYang 421005,China; 2.Institute of Fine Catalytic Synthesis,HuNan Normal University,ChangSha 410005,China)
(1.HuNan Environmental & Biologic College,HengYang 421005,China; 2.Institute of Fine Catalytic Synthesis,HuNan Normal University,ChangSha 410005,China

Abstract
Reference
Related Articles
Download: PDF (0KB)   HTML ()   Export: BibTeX or EndNote (RIS)      Supporting Info
Abstract Used lauryl amine,as well as hexadecyl trimethyl ammonium bromide as templating agent,Ti catalysts with mesoporous framework(Ti HMS) were synthesized.FT IR show that there is a weak band near 960 cm -1 ,and the intensity of this band corresponds well with the content of Ti loading.The condition of synthesising the catalysts was systemically researched.Experimetn data show:when calcining temperature is at 650℃,activating temperature at 200℃,reacting temperature between 45 and 55℃,the percent conversion of styrene approach 80% and yield of epoxy styrene get to 70%.
Service
Email this article
Add to my bookshelf
Add to citation manager
Email Alert
RSS
Articles by authors
Keywords:   
Received 2002-07-15; published 2002-07-15
Cite this article:   
ZENG Lei 1,FU Zai hui 2,YIN Du lin 2 .Synthesis and Properties of Skeleton Ti-Catalyst[J]  Chemcial Industry and Engineering, 2002,V19(4): 297-300
Copyright 2010 by Chemcial Industry and Engineering