Preparation of ZrB2 Nano-Powders by Novel Sol-Gel Technology
CHEN  Ya-Lu, HUANG  Zu-Bin, ZHANG  Mei-Yu, CHEN  Shuo, LI  Min-Min, JI  Hui-Ming
(Key Laboratory for Advanced Ceramics and Machining Technology of Ministry of Education, School of Materials Science and Engineering,
Tianjin University, Tianjin 300072, China)

Abstract
Reference
Related Articles
Download: PDF (1165KB)   HTML ()   Export: BibTeX or EndNote (RIS)      Supporting Info
Abstract A stable and homogeneous Zr-B-C mixed sol system was obtained through sol-gel process using ZrOCl2, H3BO3 and sucrose as raw materials. Citric acid (CA) was adopted as complexing agent and polyethylene glycol (PEG600) was added in the system as dispersant. The transformation of sol to gel was achieved by adding ammonia water into the mixed sol drop by drop. Near-spherical ZrB2 particles with diameter of 40 nm were synthesized by carbonthermal reduction reaction at 1 500 ℃. XRD, SEM and other analysis methods were applied to study phase composition and microstructure of the nanoparticles as prepared. The effect of CA-complexation technology on the sol was also discussed in this paper. The results showed that stable Zr-B-C mixed sol system can be obtained when the molar ratio of Zr to CA is 3; pure and phase composition controllable ZrB2 powder can be prepared by increasing the molar ratio of B to Zr; dispersibility of the ZrB2 nanoparticles was better when 1.0%PEG was added.
Service
Email this article
Add to my bookshelf
Add to citation manager
Email Alert
RSS
Articles by authors
CHEN Ya-Lu
HUANG Zu-Bin
ZHANG Mei-Yu
CHEN Shuo
LI Min-Min
JI Hui-Ming
Keywordssol-gel   citric acid   ZrB2   phase composition   nano-powder     
Received 2012-06-26;
Fund:

“Nippn Sheet Glass Foundation for Material Science and Engineering(2010-2013)”资助。

Corresponding Authors: 季惠明,电话:(033)27890485,E-mail:jihuiming@tju.edu.cn。     Email: jihuiming@tju.edu.cn
About author: 陈雅璐(1991-),女,本科生,主要从事无机纳米粉体方面的研究。
Cite this article:   
CHEN Ya-Lu, HUANG Zu-Bin, ZHANG Mei-Yu, CHEN Shuo, LI Min-Min, JI Hui-Ming.Preparation of ZrB2 Nano-Powders by Novel Sol-Gel Technology[J]  Chemcial Industry and Engineering, 2013,V30(5): 7-10
Copyright 2010 by Chemcial Industry and Engineering