助剂对加氢催化剂Ni/SiO_2结构和反应性能的影响
陶然,陈吉祥,张继炎
天津大学化工学院,天津大学化工学院,天津大学化工学院 天津300072 ,天津300072 ,天津300072
Effects of Promoters on Structure and Properties of Ni/SiO_2 Catalysts for Hydrogenation
TAO Ran,CHEN Ji-xiang,ZHANG Ji-yan (School of Chemical Engineering,Tianjin University,Tianjin 300072,China)
(School of Chemical Engineering,Tianjin University,Tianjin 300072,China

摘要
参考文献
相关文章
Download: PDF (256KB)   HTML ()   Export: BibTeX or EndNote (RIS)      Supporting Info
摘要 采用等体积浸渍法制备了含不同助剂的m 二硝基苯液相催化加氢催化剂Ni/SiO2,利用BET、XRD、TPR和活性评价等方法对催化剂的物化性质和催化性能进行了研究,考察了不同助剂对催化剂结构和反应性能的影响。试验结果表明,向NiO/SiO2催化剂中引入La2O3、K2O及Li2O助剂后提高了催化剂中镍物种的分散度及还原能力,改善了催化剂的反应性能,其中以La2O3和K2O双助剂的作用最为明显。
Service
把本文推荐给朋友
加入我的书架
加入引用管理器
Email Alert
RSS
作者相关文章
陶然
陈吉祥
张继炎
关键词m二硝基苯   m苯二胺   负载型镍基催化剂   等体积浸渍   助剂     
Abstract: A series of nickel catalyst samples supported on silica and promoted with different promoters,were prepared by incipient impregnation and used for hydrogenation of m-dinitrobenzene to m-phenylenediamine.Based on the results of nitrogen adsorption-desorption,X-ray diffraction(XRD),temperature-programmed reduction (TPR) and activity evaluation,the physico-chemical properties and catalytic performance of the catayst were investigated.It was found that promoters of La_2O_3,K_2O and Li_2O could enhance the dispersity and the reduction ability of nickel species on the catalyst of Ni/SiO_2,and so they improved the catalytic performance of the catalysts,especially double promoters of La_2O_3 and K_2O.
Keywords:   
Received 2005-05-15; published 2005-05-15
引用本文:   
陶然,陈吉祥,张继炎.助剂对加氢催化剂Ni/SiO_2结构和反应性能的影响[J].  化学工业与工程, 2005,22(3): 175-178
TAO Ran,CHEN Ji-xiang,ZHANG Ji-yan .Effects of Promoters on Structure and Properties of Ni/SiO_2 Catalysts for Hydrogenation[J].  Chemcial Industry and Engineering, 2005,22(3): 175-178
Copyright 2010 by 化学工业与工程