三维膜电极电控离子分离过程离子扩散特性研究

摘要通过阴极电沉积法在石墨芯基体上制备铁氰化镍(NiHCF)薄膜,然后组装为多排石墨芯(MRGC)膜电极系统于1mol/LKNO3溶液中测定其循环伏安(CV)曲线。重点考察了不同电极厚度与间距的MRGC基体NiHCF膜电极CV图的阴阳极峰电位分离情况,以及不同扫描速度下膜电极系统的CV图变化情况。研究结果表明,由于三维MRGC膜电极系统内部离子扩散影响,CV图的峰电位将发生偏移。随着石墨芯间距的增加电极内离子扩散阻力降低,导致CV图阴阳极峰电位差ΔEp将减小;固定石墨芯间距而增加电极厚度时电极内离子扩散阻力增加使ΔEp也随之增加;随着扫描速度的增加内扩散的影响加剧导致ΔEp增加。因此循环伏安图阴阳极峰电位的分离程度可用于三维膜电极内离子扩散的分析。

	Service

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	杨言言
	郝晓刚
	张忠林
	马旭莉
	刘世斌

关键词：电控离子分离三维膜电极循环伏安法

Abstract： Nickel hexacyanoferrate(NiHCF)thin films were synthesized on graphite core substrates by cathodically deposition,and then were assembled as multi-row graphite core(MGRC)film electrodes.The cyclic voltammetry(CV)of the MGRC film electrodes was determined in 1 mol·L-1 KNO_3 solution.The separation(ΔE_p)between the anodic and cathodic peak potentials in the CV curves of MRGC film electrodes with different thickness and spacing was investigated,and the change of CV curves at different scan rates was also measured.Experimental results show that,the excursion of the peak potential of CV curves is caused by ion diffusion in three-dimensional MRGC film electrodes;the ion diffusion resistance in electrode decreases with the increase of thickness of graphite matrix,this leads to the decrease of ΔE_p with the increase of spacing between graphite cores.With the increase of the scan rate,ΔE_p is also increased because of the inner diffusion in the film electrodes.Therefore,the separation degree between the anodic and cathodic peak potentials in the CV curves can be used to analyze the ion diffusion in three-dimensional film electrodes.

Keywords：

Received 2009-07-15; published 2009-07-15

引用本文:

杨言言;郝晓刚;张忠林;马旭莉;刘世斌;.三维膜电极电控离子分离过程离子扩散特性研究[J]. 化学工业与工程, 2009,26(4): 283-287

YANG Yan-yan,HAO Xiao-gang,ZHANG Zhong-lin,MA Xu-li,LIU Shi-bin.Ion Diffusion in Three-Dimensional Film Electrodes for ECIS Process[J]. Chemcial Industry and Engineering, 2009,26(4): 283-287

[1]	RASSAT S D,SUKAMTO J H,ORTH R J,et al.Development of an electrically switched ion exchange processfor selectiveionseparations[J].Sep Purifi Technol.1999,15(3):207-222
[2]	郝晓刚,张忠林,刘世斌,等.电活性铁氰化镍离子交换膜的制备及应用[P].中国专利.中国200410012195.8.2004-03-20
[3]	JEERAGE K M,SCHWARTZ D T.Characterization of cathodically deposited nickel hexacyanoferrate forelectrochemically switched ion exchange[J].Sep Sci Technol.2000,35(15):2375-2392
[4]	HAO X G,SCHWARTZ D T.Tuning intercalation sites in nickel hexacyanoferrate using lattice nonstoichiometry[J].Chem Mater.2005,17(23):5831-5836
[5]	郝晓刚,马旭莉.电化学控制离子交换(分离)膜的制备、结构与性能[J].功能材料,2007,38(增):2721-2726
[6]	HAO X G,GUO J X,ZHANG Z L,et al.Electrochemically switched ion exchange performances of capillary deposited nickel hexacyanoferrate thin films[J].Trans Nonferrous Met Soc China.2006,16(3):556-561
[7]	LILGA MA,ORTHRJ,SUKAMTOJ P H,et al.Cesium separation using electrically switchedion exchange[J].Sep Purifi Technol.2001,24(3):451-466
[8]	鞠健,郝晓刚,张忠林,等.电沉积NiHCF薄膜在碱土金属溶液中的电控离子分离性能[J].无机材料学报,2008,23(6):1115-1120
[9]	GREEN-PEDERSEN H,KORSHIN G V.Separation of cesiumfrom high ionic strength solutions using a cobalt hexacyanoferrate-modified graphite electrode[J].Environ Sci Technol.1999,33(15):2633-2637
[10]	CHEN W,XIAX H.Highly stable nickel hexacyanoferrate nanotubes for electrically switched ion exchange[J].Adv Funct Mater.2007,17(15):2943-2948
[11]	李永国,郝晓刚,张忠林,等.三维多孔石墨基NiHCF电控离子分离膜电极制备及表征[J].稀有金属材料与工程,2007,36(增3):211-216
[12]	REYES GJ,MEDINAJ A,JEERAGE K M,et al.High capacity SiO2-graphite composite electrodes with chemically incorporated metal MHCFs for electrochemically switched alkaline cation exchange[J].J Electrochem Soc,2004,151(9):D87-D92
[13]	LINY H,CUI XL.Electrosynthesis,characterization,and application of novel hybrid materials based on carbon nanotube-polyaniline-nickel hexacyanoferrate nanocomposites[J].Mater Chem.2006,16(6):585-592
[14]	李永国,郝晓刚,马旭莉,等.碳纤维/石墨基电控离子分离NiHCF膜电极制备与表征[J].功能材料,2008,39(6):949-952
[15]	郝晓刚,郭金霞,张忠林,等.电沉积NiHCF薄膜电控离子交换性能研究[J].化工学报,2005,56(12):2380-2386
[16]	张玫,郝晓刚,马旭莉,等.石墨基体NiHCF薄膜的离子交换性能[J].稀有金属材料与工程,2006,35(增2):249-253