海藻酸钙海绵及其载银后的性能研究

摘要

采用机械搅拌发泡，内源凝胶法，制备了多孔海藻酸钙海绵及负载纳米银海藻酸钙海绵。实验结果如下：乙醇处理湿凝胶可加速干燥过程，保留海绵孔道结构；乙醇-甘油水溶液后处理，可获得具有一定柔韧性的海藻酸钙海绵；海绵经AgNO₃溶液浸渍，乙醇-甘油水溶液处理，80 ℃干燥，可得到载纳米银海藻酸钙海绵；改变乙醇-甘油水溶液含量，可调节海绵的吸液率、保液率和力学性能；载纳米银海藻酸钙海绵对金黄色葡萄球菌和大肠杆菌均具有良好的抑菌性能。

	Service

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	王康
	郝艳丽

关键词：海藻酸；海绵；纳米银；抑菌性能

Abstract：

Porous calcium alginate (ALG-Ca) sponges with or without silver nanoparticles (AgNPs) were prepared by tailoring hydrogel to incorporate enough air and internal gelling method. The experiment result was as follows: ALG-Ca wet sponge was disposed by using absolute ethyl alcohol to accelerate the process of drying and remain the porous structure to achieve ALG-Ca desiccated sponge, then ALG-Ca sponge with excellent flexibility was obtained through impregnating ALG-Ca desiccated sponge into alcohol-glycerol aqueous solution. Moreover, ALG-Ca sponges were immerged into AgNO₃ solution, then impregnated into alcohol-glycerol aqueous and dried at 80 ℃ to prepare AgNPs-loaded ALG-Ca sponges. The change of water solution including various alcohol and glycerol has an influence on the liquid absorption, liquid preservation and mechanical properties of Ca-ALG sponges. AgNPs-loaded ALG-Ca sponges showed good antibacterial capability against both Staphylococcus aureus and Escherichia coli.

Keywords： alginate； sponges； silver nanoparticles； antibacterial capability

Received 2015-11-17;

Fund:

国家自然科学基金资助项目（21276190）。

Corresponding Authors: 王康,E-mail:wangk72@tju.edu.cn。 Email: wangk72@tju.edu.cn

About author: 王康(1972-),女,副教授,从事金属氧化物与生物材料的研究。

引用本文:

王康, 郝艳丽.海藻酸钙海绵及其载银后的性能研究[J]. 化学工业与工程, 2017,34(3): 18-23

Wang Kang, Hao Yanli.Study on the Capacity of Calcium Alginate Sponge with or Without Silver Nanoparticles[J]. Chemcial Industry and Engineering, 2017,34(3): 18-23

[1] 秦益民, 朱长俊, 冯德明, 等. 海藻酸钙医用敷料与普通棉纱布的性能比较[J]. 纺织学报, 2007, 28(3): 45-48 Qin Yimin, Zhu Changjun, Feng Deming, et al. Comparison of the properties of calcium alginate wound dressing and cotton gauze[J]. Journal of Textile Research, 2007, 28(3): 45-48(in Chinese)
[2] 何瑞华, 张传杰, 赵瑾朝, 等. 柔性海藻酸钙海绵伤口敷料的制备及性能[J]. 功能材料, 2013, 44(11): 1 574-1 578 He Ruihua, Zhang Chuanjie, Zhao Jinchao, et al. Preparation and properties of flexible calcium alginate sponges as a novel wound dressing[J]. Function Materials, 2013, 44(11): 1 574-1 578(in Chinese)
[3] 张传杰, 徐琪, 熊春华, 等. 海藻酸钙海绵的结构与性能[J]. 高分子材料科学与工程, 2012, 28(9): 24-27 Zhang Chuanjie, Xu Qi, Xiong Chunhua, et al. Properties and structure of calcium alginate sponge[J]. Polymer Material Science and Engineering, 2012, 28(9): 24-27(in Chinese)
[4] 郝晓丽. 海藻酸钙冻干膜及海藻酸钙基互穿网络膜材料的制备与性能研究[D]. 山东青岛: 青岛大学, 2010 Hao Xiaoli. Preparation and characterization of free-dried calcium alginate and calcium alginate-based IPN membranes[D]. Shandong Qingdao: Qingdao University, 2010(in Chinese)
[5] Andersen T, Melvik J E, Gåserød O, et al. Ionically gelled alginate foams: Physical properties controlled by operational and macromolecular parameters[J]. Biomacromolecules, 2012, 13: 3 703-3 710
[6] Andersen T, Melvik J E, Gåserød O, et al. Ionically gelled alginate foams: Physical properties controlled by type, amount and source of gelling ions[J]. Carbohydrate Polymers, 2014, 99: 249-256
[7] 张帆. 纳米银海藻酸钙抗菌敷料: 中国, 200610053877.2[P]. 2007-03-28
[8] Fan L, Zhu H, Zheng H, et al. Structure and properties of blend fibers prepared from alginate and konjac glucomannan[J]. Journal of Applied Polymer Science, 2007, 106: 3 903-3 907
[9] Praus P, Turicová M, Machovi? V, et al. Characterization of silver nanoparticles deposited on montmorillonite[J]. Applied Clay Science, 2010, 49(3):341-345
[10] Parveen A, Ali T, Wahid M, et al. Facile biological approach for immobilization, physicochemical characterization and antibacterial activity of noble metals nanocomposites[J]. Materials Letters, 2015, 148: 86-90
[11] Malachová K, Praus P, Pavlí?ková Z, et al. Activity of antibacterial compounds immobilised on montmorillonite[J]. Applied Clay Science, 2009, 43(3/4):364-368
[12] Lee Y J, Lyoo W S. Preparation and characterization of high-molecular-weight atactic poly(vinyl alcohol)/sodium alginate/silver nanocomposite by electrospinning[J]. Journal of Polymer Science, 2009, (47): 1 916-1 926
[13] Marie A P, Sekar S, Sankar S, et al. Evaluation of biocomposite films containing alginate and sago starch impregnated with silver nano particles[J]. Carbohydrate Polymers, 2012, 90: 717-724
[14] 王春来, 关静, 田丰. 海藻酸钠光化学还原法制备纳米银[J]. 材料导报B: 研究篇, 2015, 29(8): 36-39 Wang Chunlai, Guan Jing, Tian Feng. Preparation of nano-silver by photo-reduction method using sodium alginate[J]. Materials Review B: Research Articles, 2015, 29(8): 36-39(in Chinese)
[15] Yang J, Pan J. Hydrothermal synthesis of silver nanoparticles by sodium alginate and their applications in surface-enhanced Raman scattering and catalysis[J]. Sci Verse Science Direct, 2012, 60: 4 753-4 758
[16] 陈建波, 李启厚, 李玉虎, 等. 以丙三醇为还原剂的沉淀转化法制备超细银粉[J]. 粉末冶金材料科学与工程, 2013, (6): 874-881 Chen Jianbo, Li Qihou, Li Yuhu, et al. Preparation of ultra-fine silver powders by precipitation-transformation method using glycerol as reductant[J]. Materials Science and Engineering of Powder Metallurgy, 2013, (6): 874-881(in Chinese)
[17] Jovanovi? ?, Stojkovska J, Obradovi? B,et al. Alginate hydrogel microbeads incorporated with Ag nanoparticles obtained by electrochemical method[J]. Materials Chemistry & Physics, 2012, 133(1): 182-189
[18] Eghbalifam N, Frounchi M, Dadbin S. Antibacterial silver nanoparticles in polyvinyl alcohol/sodium alginate blend produced by gamma irradiation[J]. International Journal of Biological Macromolecules, 2015, 80: 170-176