无外加表面活性剂的苯乙烯悬浮聚合

摘要

针对传统悬浮聚合制备聚苯乙烯颗粒粒径分布宽、有效粒子收率低的问题,采用过硫酸铵/磷酸钙复合分散剂体系,在无外加表面活性剂情况进行苯乙烯悬浮聚合,制备了聚苯乙烯珠粒。通过对聚合稳定性、聚苯乙烯珠粒粒径及分布的测定与分析,考察了磷酸钙、过硫酸铵的用量及比例对悬浮聚合的影响,并分析了过硫酸胺对悬浮聚合的分散稳定机理。结果表明,当过硫酸铵和磷酸钙的用量分别为单体质量的0.01%和1.00%时,悬浮聚合体系稳定,得到的粒子透明性好,平均粒径为1.35 mm,粒径分布窄;通过改变过硫酸铵和磷酸钙的用量,可以调节聚苯乙烯珠粒的平均粒径。

	Service

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	赵颖
	陈苏
	许涌深
	袁才登

关键词：悬浮聚合；苯乙烯；分散剂；过硫酸铵；粒径分布

Abstract：

Polystyrene particles prepared by suspension polymerization are widely used, however, the size distribution of polystyrene particles synthesized by traditional suspension polymerization is not narrow enough and the yield of the desired particles is low. In order to solve these problems, suspension polymerization without surfactant was used to prepare polystyrene particles. The dispersion system of ammonia persulfate/tricalcium phosphate (APS/TCP) was used as stabilizing agents in the preparation of polystyrene particles with suspension polymerization. The effects of dispersion system of APS/TCP on stability of suspension polymerization and the size distribution of polystyrene particles were discussed. In additional, the dispersion mechanism of APS/TCP system was analyzed. The results show that when the quantity of APS is 0.01% and that of TCP is 1.00% of the total monomer weight, suspension polymerization is stable, polystyrene particles are with good transparency, and the monodispersed polystyrene particles with average diameter of 1.35 mm can be obtained. The particle size and its distribution can be controlled by changing the amount of ammonium persulfate and tricalcium phophate.

Keywords： suspension polymerization； styrene； dispersant； ammonium persulfate； particle size distribution

Received 2013-05-14;

Corresponding Authors: 袁才登,E-mail:cdyuan1209@sina.com。 Email: cdyuan1209@sina.com

About author: 赵颖(1986-),女,硕士研究生,主要从事非均相聚合研究。

引用本文:

赵颖, 陈苏, 许涌深, 袁才登.无外加表面活性剂的苯乙烯悬浮聚合[J]. 化学工业与工程, 2015,32(4): 24-29

Zhao Ying, Chen Su, Xu Yongshen, Yuan Caideng.Suspension Polymerization of Styrene without Extra-Surfactant[J]. Chemcial Industry and Engineering, 2015,32(4): 24-29

[1] 周建, 罗学刚. 可发性聚苯乙烯(EPS)悬浮聚合研究进展[J]. 广东化工, 2004, (10): 34-37 Zhou Jian, Luo Xuegang. Process in suspension polymerization of expanded polystyrene[J]. Guangdong Chemical Industry, 2004, (10): 34-37(in Chinese)
[2] 董绍胜, 魏月贞, 白水平, 等. 高分子材料科学与工程[M]. 北京: 化学工业出版社, 2000
[3] 杨珍. 苯乙烯聚合物的合成、表征以及引发剂活性的测试[D]. 天津:天津大学, 2007 Yang Zhen. Synthesis, characterization and test of trigger agent activity of styrene polymers[D]. Tianjin: Tianjin University, 2007(in Chinese)
[4] 积水化成品工业株式会社. 生产聚苯乙烯型珠粒和可发泡聚苯乙烯型珠粒: 日本, 96104499[P]. 1996-12-25
[5] Wolters D, Meyer-Zaika W, Bandermann F. Suspension polymerization of styrene with pickering emulsifiers[J]. Macromolecular Materials and Engineering, 2001, 286(2): 94-106
[6] 梁博, 韩凤兰, 杨鹏元. 分散剂对悬浮制备聚苯乙烯的影响及形貌分析[J]. 中国组织工程研究与临床康复, 2010, 14(47): 8 805-8 808 Liang Bo, Han Fenglan, Yang Pengyuan. Effect of dispersant on suspension preparation to prepare polystyrene and morphology analysis[J]. Chinese Journal of Clinical Rehabilitation, 2010, 14(47): 8 805-8 808(in Chinese)
[7] 张建丽, 迟长龙. 苯乙烯悬浮聚合力度的控制[J]. 河南工程学院学报: 自然科学版, 2008, 20(1): 57-58 Zhang Jianli, Chi Changlong. Control of styrene suspension polymerization efforts[J]. Henan Institute of Engineering: Science and Technology, 2008, 20(1): 57-58(in Chinese)
[8] 王俏, 张玉琦, 刘勇. 苯乙烯悬浮聚合工艺条件优化[J]. 化学与生物工程, 2010, 27(4): 71-73 Wang Qiao, Zhang Yuqi, Liu Yong. Optimization of styrene suspension polymerization process[J]. Chemical and Biological Engineering, 2010, 27(4): 73-73(in Chinese)
[9] 徐昊垠, 董春明. 悬浮聚合制备微米级聚苯乙烯微球[J]. 化工生产与技术, 2010, 17(3): 24-26 Xu Haoyin, Dong Chunming. Preparation of micron polystyrene microspheres by suspension polymerization[J]. Chemical Production and Technology, 2010, 17(3): 24-26(in Chinese)
[10] Yang W T, Ko T H, Wang S C, et al. Preparation of polystyrene/clay nanocomposite by suspension and emulsion polymerization[J]. Polymer Composite, 2008, 29(4): 409-414
[11] 高海涛, 马小华. 聚合时间、分散介质的配比对聚苯乙烯高分子微球表征的影响[J]. 化学工程与装备, 2013, (1): 5-6 Gao Haitao, Ma Xiaohua. Effects of polymerization time, ratio of the dispersion medium on characterization of the polystyrene microspheres[J]. Chemical Engineering and Equipment, 2013, (1): 5-6(in Chinese)
[12] Schellenberg J. Effects of styrene oligomers and polymers on the suspension polymerization behavior and properties of expandable polystyrene[J]. Journal of Applied Polymer Science, 2008, 110(1): 453-458
[13] Yang J, Mao X, Zhang Q, et al. One-Step preparation of black polystyrene particles via in situ suspension polymerization[J]. Polymer Engineering and Science, 2011, 51(2): 294-301
[14] William N M. The mechanism of extender action by potassium persulfate in the suspension polymerization of styrene [J]. Journal of Applied Polymer Science, 1971, 15(4): 867-888
[15] 张茂根, 翁志学, 黄志明, 等. 颗粒统计平均粒径及其分布的表征[J]. 高分子材料科学与工程, 2000, 16(5): 1-4 Zhang Maogen, Weng Zhixue, Huang Zhiming, et al. Statistical average size of particles and characterization of size distribution[J]. Polymer Materials Science and Engineering, 2000, 16(5): 1-4(in Chinese)