化学工业与工程 2014, Vol. 31 Issue (5) :70-73    DOI: doi: 10.13353/j.issn.1004.9533.2014.05.013
过程与设备 最新目录 | 下期目录 | 过刊浏览 | 高级检索 << | >>
卡纸涂层对EB固化直接真空镀铝工艺的影响
余振华1,詹建波1,郑迪生2,李赓1,布宁3,李建3,胡信洋3,薛守成2
(1红云红河烟草(集团)有限责任公司,昆明 650202; 2博源科技材料(烟台)有限公司,山东 烟台 264670;3万国纸业太阳白卡纸有限公司,山东 兖州 272100)
Influence of Coating Composition of Paperboard on Electron Beam Curing and Vacuum Aluminizing Process
YU  Zhen-Hua,1 ZHAN  Jian-Bo1, ZHENG  Di-Sheng2, LI  Geng1, BU  Ning3, LI  Jian3, HU  Xin-Yang3, XUE  Shou-Cheng2
(1Hongyunhonghe Tobacco (Group) Co. Ltd., Kunming 650202,China; 2Boyuan Technology Materials(Yan Tai)Co. Ltd., Yantai  264670, China; 3International Paper and Sun Cartoon Board Co. Ltd., Yanzhou 272100, China)

摘要
参考文献
相关文章
Download: PDF (1485KB)   HTML ()   Export: BibTeX or EndNote (RIS)      Supporting Info
摘要 通过改变卡纸涂布量和涂层中瓷土与碳酸钙的比例,研究了卡纸涂层对电子束固化直接真空镀铝工艺的影响。结果表明,随卡纸涂料量提高,表征涂层开放程度的油墨吸收性也随之提高,但卡纸的耐折性能则下降,电子束(EB)固化预涂料涂布量也随之增大;卡纸涂层材料中颜料的组成对卡纸性能及EB固化涂料预涂量有影响,随着颜料中瓷土含量降低,碳酸钙含量提高,涂层的开放程度提高,纸张光泽度下降。
Service
把本文推荐给朋友
加入我的书架
加入引用管理器
Email Alert
RSS
作者相关文章
余振华
詹建波
郑迪生
李赓
布宁
李建
胡信洋
薛守成
关键词电子束固化   直接真空镀铝   卡纸   颜料     
Abstract: The influence of coating composition of paperboard on electron beam curing and vacuum aluminizing process was studied by changing the pigment weight and its composition (the ratio of clay to calcium carbonate). The results show that with the increasing of the coating weight on paperboard, K&N (the parameter for ink absorbency of paper board, which characterizes the openness of the paper coatings) increases, the folding performance are reduced and the coating weight for electron beam curing increases. The pre-coated weight of electron beam curing coating was also depended on the ratio of clay to calcium carbonate. With decreasing the clay content and increasing the calcium carbonate content, the openness of the coatings was increased and the coating gloss was reduced.
Keywordselectron beam curing;   vacuum aluminizing   paperboard   pigment     
Received 2014-05-20;
Corresponding Authors: 余振华,E-mail:16929268@qq.com。     Email: 16929268@qq.com
About author: 余振华(1973-),男,工程师,主要从事卷烟产品开发与烟用材料应用研究。
引用本文:   
余振华, 詹建波, 郑迪生, 李赓, 布宁, 李建, 胡信洋, 薛守成.卡纸涂层对EB固化直接真空镀铝工艺的影响[J].  化学工业与工程, 2014,31(5): 70-73
YU Zhen-Hua, ZHAN Jian-Bo, ZHENG Di-Sheng, LI Geng, BU Ning, LI Jian, HU Xin-Yang, XUE Shou-Cheng.Influence of Coating Composition of Paperboard on Electron Beam Curing and Vacuum Aluminizing Process[J].  Chemcial Industry and Engineering, 2014,31(5): 70-73