硬脂酸单甘酯模板法制备介孔硅材料及功能化

摘要以硬脂酸单甘酯非离子表面活性剂为模板剂，采用模板法自组装合成了具有介孔结构的新型纯硅基材料，并在此基础上添加镁铝改性合成了新型功能化介孔材料，采用XRD和N2物理吸附脱附等方法进行表征，结果表明，活性物种进入了介孔硅的骨架并保持了介孔结构特征，活性物种在母体表面分散较好。以十八酸和丙三醇的酯化反应作为探针反应考察其催化性能，结果表明，功能化介孔材料有较好的酯化反应活性。

	Service

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	刘莉
	陈英
	王华
	韩金玉

关键词：介孔硅材料脂肪酸单甘酯模板法功能化催化

Abstract： A novel mesoporous silica material have been synthesized by self-assembly route.Subsequently，the modification of the material with metal ions was performed.X-ray diffraction，N₂ adsorptiondesorption isotherms and so on were employed to characterize the mesoporous materials.The characterization results indicated that the resultant mesoporous nanocomposites could keep mesoporous structure properties well and the active species could fully disperse on the channel surface of the host.The esterification reaction of stearic acid and glycerol was employed as a probe reaction to evaluate the catalytic performance of the mesoporous material.The results suggested the modified mesoporous material exhibited good performance in this reaction.

Keywords： mesoporous material monoglyceric stearate template route modification catalysis

Received 2011-09-11;

Fund:

国家自然科学基金资助项目（20776109，21076152）；教育部博士点基金（20100032110018）。

Corresponding Authors: 王华 Email: tjuwanghua@tju.edu.cn

About author: 刘莉（1987-），女，天津人，硕士研究生，研究方向为功能化介孔材料的制备及应用。

引用本文:

刘莉, 陈英, 王华, 韩金玉.硬脂酸单甘酯模板法制备介孔硅材料及功能化[J]. 化学工业与工程, 2012,29(2): 1-8

LIU Li, CHEN Ying, WANG Hua, HAN Jin-Yu.Synthesis and Modification of Mesoporous Materials by Monoglyceric Stearate Template Route[J]. Chemcial Industry and Engineering, 2012,29(2): 1-8

[1]	CORMA A，NAVARRO M T，PARIENTE J PSynthesis of an ultralarge pore titanium silicate isomorphous to MCM41 and its application as a catalyst for selective oxidation of hydrocarbons［J］.Chem Commun，1994，（1）：147-148
[2]	CORMA A，FORNES V，NAVARRO M T，et al.Acidity and stability of MCM41 crystalline aluminosilicates[J].J Catal.1994,148(2):569-574
[3]	REDDY K M，MOUDRAKOVSKI I，SAYARI A.Synthesis of mesoporous vanadium silicate molecular sieves［J］.Chem Commun,1994，1 059-1 060
[4]	MASCHMEYER T，REY F，SANHAR G，et al.Heterogeneous catalysts obtained by grafting metallocene complexes onto mesoporous silica[J].Nature.1995,378:159-162
[5]	BRANTON P J，HALL P G，SING K S W，et al.Physisorption of argon，nitrogen and oxygen by MCM41，a model mesoporous adsorbent［J］.Faraday Trans，1994，90：2 965-2 9
[6]	KIM J M，KWAK J H，JUN S，et al.Ionexchange and thermalstability of MCM4l［J］.J Phys Chem，1995，99（45）：16 742-16 747
[7]	WU C，BEIN T.Conducting polyaniline filaments in a mesoporous channel host[J].Science.1994,264:-
[8]	WU C，BEIN T.Conducting carbon wires in ordered，nanometersized channels[J].Science.1994,266:-
[9]	CORMA A.From microporous to mesoporous molecular sieve materials and their use in catalysis［J］.Chem Rev，1997，97(6）：2 373-2 420
[10]	SZEGEDI A，KONYA Z，MEHN D.Spherical mesoporous MCM41 materials containing transition metals：Synthesis and characterization[J].Appl Catal A：Gen.2004,272(1/2):257-266
[11]	YUAN S，SHENG Q，ZHANG J.Synthesis of La3+ doped mesoporous titania with highly crystallized walls[J].Micropor Mesopor Mater.2005,79(1/3):93-99
[12]	GAGO S，ZHANG Y，SANTOS A M.Synthesis and characterization of a manganese（II）acetonitrile complex supported on functionalized MCM41[J].Micropor Mesopor Mater.2004,76(1/3):131-136
[13]	SELVARAJ M，SINHA P K，LEE K.Synthesis and characterization of MnMCM41 and ZrMnMCM41[J].Micropor Mesopor Mater.2005,78(2/3):139-149
[14]	沈绍典.多头季铵盐表面活性剂导向下新结构介孔分子筛的合成与表征［D］.上海：复旦大学，2003
[15]	陈英.新型酸碱双功能介孔材料的合成、表征及催化性能研究［D］.天津：天津大学，2008
[16]	BOCCUTI M R，RAO K M，ZECCHINA A，et al.Spectroscopic characterization of silicalite and titaniumsilicalite[J].Stud Surf Sci Catal.1989,48:133-144
[17]	冯春祥，宋永才，谭自烈.元素有机化合物及其聚合物［M］.长沙：国防科技大学出版社，1999