新型偶联剂和特种固化剂对铜-环氧导电涂料的影响

摘要在铜-环氧导电涂料的制备中,应用了一种新型偶联剂A和特种固化剂B。研究发现:当偶联剂用量为铜粉质量的2%~3%和固化剂用量范围在20%~40%时,对试样进行微观机理分析的结果表明固化剂B的作用不限于交联固化,与偶联剂A之间存在协同效应,当与偶联剂相互配合用量合适时,才能制备出低电阻、导电稳定、涂膜性能好的涂料。

	Service

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	鲁彦玲
	施冬梅
	杜仕国

关键词：偶联剂固化剂铜粉环氧树脂

Abstract： A new coupling agent and a new binding agent were used in developing copper-epoxy resin conductive paint.The results showed that the conductive properties was the best as the coupling agent,binding agent was 2%—3%,20%—40%,respectively.And the effect of the binding agent was not only binding but also some cooperation with copper powder.