制备条件对磷酸铁锂电化学性能的影响

摘要采用辅助微波加热的方法,制得了粒子较细、粒径分布窄的LiFePO4/C化合物。利用X射线衍射(XRD)、扫描电镜(SEM)和透射电镜(TEM)对所得样品的晶体结构、表面形貌和粒径分布进行了分析研究。试验表明,采用该反应方法有利于控制产物的形貌和粒径。用LiFePO4/C作正极材料进行了电池的充放电和循环伏安测试,结果显示,材料中锂离子的充放电平台相对锂电极电位为3.5 V左右,首次放电量为151 mA.h/g,表现出了良好的循环性能和高倍率性能。

	Service

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	刘晓亮
	单忠强
	张磊
	田建华

关键词：锂离子电池正极材料磷酸铁锂微波加热

Abstract： The fine-particle electroactive material LiFePO_4/C was synthesized by microwave heating,and the samples were characterized by X-ray diffraction,SEM and TEM.The reaction conditions was favored for offering some control of the product morphology and particle size.The results of charge-discharge test and cyclic voltammetry of LiFePO_4/C showed a lithium insertion plateau was around 3.5 V vs Li, with a specific capacity of 151 mA·h/g.Excellent electrochemical reversibility and cycling stability were achieved.

Keywords： lithium ion battery cathode materials lithium iron phosphate microwave heating

Received 2008-11-15; published 2008-11-15

引用本文:

刘晓亮;单忠强;张磊;田建华;.制备条件对磷酸铁锂电化学性能的影响[J]. 化学工业与工程, 2008,25(6): 471-474

LIU Xiao-liang,SHAN Zhong-qiang,ZHANG Lei,TIAN Jian-hua.Effects of Experiment Conditions on Electrochemical Performance of Lithium Iron Phospho-Olivine[J]. Chemcial Industry and Engineering, 2008,25(6): 471-474

[1]	PADHI A K,NANJUNDASWAMY K S,GOODENOUGH JB.Phospho-olivines as positive-electrode materials forrechargeable lithium batteries[J].J Electrochem Soc.1997,144(4):1-
[2]	YANG S F,ZAVALIJ P Y,WHITTINGHAM M S.Hydrothermal synthesis of lithium iron phosphate cathodes[J].Electrochemistry Communication.2001,3:505-508
[3]	TAKAHASHI M,TOBISHIMA S,TAKEI K,et al.Characterization of LiFePO4as the cathode material forrechargeable lithium batteries[J].J Power Sources.2001,97/98:508-511
[4]	PIER P P,DANIELA Z,MAURO P.Improvedelectrochemical performance of a LiFePO4-based compositecathode[J].Electrochimica Acta,2001,46(23):3 517-3 523.
[5]	YANG S F,SONG Y N,PETER Y Z,et al.Reactivity,stability and electrochemical behavior of lithium ironphosphates[J].Electrochemistry Communication,2002,4(3):239-244.
[6]	ARNOLD G,GARCHE J,HEMMER R,et al.Fine-particle lithium iron phosphate LiFePO4synthesized by anew low-cost aqueous precipitation technique[J].J PowerSources,2003,119/121:247-251.
[7]	MASATAKA W.Recent developments in lithium ionbatteries[J].Material Science and Engineering,2001,R33:109-134.
[8]	CHUNG S Y,BLOKING J T,CHING Y M.Electronicallyconductive phospho-olivines as lithium storage electrodes[J].Nature Mater,2002,2:123-128.
[9]	YAMADA A,HOSOYA M,CHUNG S C,et al.Olivine-type cathodes achievements and problems[J].J PowerSources,2003,119/121:232-238.
[10]	TAKAHASHI M,TOBISHIMA S,TAKEI K,et al.Reaction behavior of LiFePO4as a cathode material forrechargeable lithium batteries[J].Solid State Ionics.2002,148(3/4):283-289