耐盐降失水剂AMPS/DMAA/IA的合成及其性能评价

摘要

针对目前降失水剂黏度大、易增稠、抗盐能力差等问题，以2-丙烯酰胺基-2甲基丙磺酸（AMPS）、N，N-二甲基丙烯酰胺（DMAA）、衣康酸（IA）为聚合单体，采用水溶液自由基聚合方法合成了适用于海水水泥浆体系的降失水剂AMPS/DMAA/IA。通过红外光谱分析，各单体成功参与聚合反应，经热重分析，三元共聚物AMPS/DMAA/IA耐温可达320℃。经水泥浆性能测试表明，该降失水剂具有优良的降失水性能，抗盐可达饱和；在海水水泥浆体系稠化曲线平稳，无"鼓包"、"包芯"现象；低温下，随着加量增加，对水泥石抗压强度影响较小，无超缓凝现象，在海水水泥浆中具有良好的综合性能。

	Service

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	喻文娟
	郭锦棠
	郭春
	王美玉
	樊金杰
	田晶

关键词：降失水剂抗盐海水水泥浆抗压强度

Abstract：

Fluid loss additives (FLAs) have the feature of high viscosity, thus increasing the consistence of cement slurry. Moreover, some FLAs exhibit poor salt-tolerant ability. Aimed at above problems, a new fluid loss additive (FLA) AMPS/DMAA/IA was synthesized through free radical aqueous solution copolymerization with the monomers of 2-acrylamido-2-methyl-propane sulphonic acid (AMPS), N,N-dimethyl-acrylamide (DMAA) and itaconic acid. The structure of the copolymer was identified by FTIR analysis. The thermogravimetry analysis showed that the terpolymer was stable when temperature was below 320℃. The polymer exhibits excellent fluid loss control ability and can be available in saturated brine. The undesired phenomenon such as "abnormal gel" or "false set" was not observed in the thickening test. What's more, the dosage of the terpolymer exerts little effect on the compressive strength of cement stone at low temperature. The far delayed solidification was not presented. It is established that the terpolymer AMPS/DMAA/IA possesses good integrated performance in sea-water cement slurry system.

Keywords： fluid loss additive； salt-resistance； sea water； cement slurry； compressive strength

Received 2016-03-23;

Fund:

天津市自然科学基金（15JCYBJC21100）。

Corresponding Authors: 郭锦棠,E-mail:jtguo@tju.edu.cn。 Email: jtguo@tju.edu.cn

About author: 郭锦棠(1968-),女,博士,教授,现从事油田化学品方面的研究。

引用本文:

喻文娟, 郭锦棠, 郭春, 王美玉, 樊金杰, 田晶.耐盐降失水剂AMPS/DMAA/IA的合成及其性能评价[J]. 化学工业与工程, 2018,35(1): 45-50

Yu Wenjuan, Guo Jintang, Guo Chun, Wang Meiyu, Fan Jinjie, Tian Jing.Synthesis and Performance Evaluation of Salt-Resistant Fluid Loss Additive AMPS/DMAA/IA[J]. Chemcial Industry and Engineering, 2018,35(1): 45-50

[1] 刘崇建,黄柏宗,徐同台,等.油气井注水泥理论与应用[M].北京:石油工业出版社,2001 Liu Changjian,Huang Boanng, Xu Tongtai, et al. The theory and application of the primary cementing[M]. Beijing:Petroleum Industry Press, 2001(in Chinese)
[2] 周明明. 适用于巨厚盐膏层的高密度水泥浆体系研究[D]. 湖北荆州:长江大学,2013 Zhou Mingming. Research on high density cement slurry system apply to thick salt-gypsum[D]. Hubei Jingzhou:Yangtze University, 2013(in Chinese)
[3] 薛燕. 油井水泥降失水剂的研究与应用[J]. 橡塑资源利用, 2008, 1:33-37 Xue Yan. Research and application of fluid loss additives for oil-well cement[J]. Rubber & Plastics Resources Utilization, 2008, 1:33-37(in Chinese)
[4] Guo S, Bu Y. Synthesis and application of 2-acrylamido-2-methyl propane sulfonic acid/acrylamide/N, -dimethyl acrylamide/maleic anhydride as N a fluid loss control additive in oil well cementing[J]. Journal of Applied Polymer Science, 2013, 127(5):3302-3309
[5] 郭锦棠, 卢海川, 靳建州,等. 新型耐温抗盐降失水剂的合成与测试[J]. 天津大学学报:自然科学与工程技术版, 2012, 45(11):1001-1006 Guo Jintang, Lu Haichuan, Jin Jianzhou, et al. Synthesis and test of novel temperature-resistant and salt-tolerant fluid loss additive[J]. Journal of Tianjin University, 2012, 45(11):1001-1006(in Chinese)
[6] Tiemeyer C, Plank J. Synthesis, characterization, and working mechanism of a synthetic high temperature (200℃) fluid loss polymer for oil well cementing containing allyloxy-2-hydroxy propane sulfonic (AHPS) acid monomer[J]. Journal of Applied Polymer Science, 2013, 128(1):851-860
[7] Plank J, Brandl A, Zhai Y, et al. Adsorption behavior and effectiveness of poly(N,N-dimethylacrylamide-co-Ca2-acrylamido-2-methylpropanesulfonate) as cement fluid loss additive in the presence of acetone-formaldehyde-sulfite dispersant[J]. Journal of Applied Polymer Science, 2006, 102(5):4341-4347
[8] Guo S, Bu Y. Synthesis and application of 2-acrylamido-2-methyl propane sulfonic acid/acrylamide/N,N-dimethyl acrylamide/maleic anhydride as a fluid loss control additive in oil well cementing[J]. Journal of Applied Polymer Science, 2013, 127(5):3302-3309
[9] 郭锦棠,卢海川,刘硕琼,等. 新型固井降失水剂HTF-200C[J]. 石油勘探与开发, 2012, 39(3):359-364 Guo Jintang, Lu Haichuan, Liu Shuoqiong, et al. The novel fluid loss additive HTF-200C for oil field cementing[J]. Petroleum Exploration and Development, 2012, 39(3):359-364(in Chinese)
[10] 刘鹭. 水基钻井液抗高温温度保护剂和降失水剂研究[D]. 成都:西南石油大学, 2014 Liu Lu. The Research on temperature-tolerant protective agent and fluid loss additive in drill fluid[D]. Chengdu:Southwest Petroleum University, 2014(in Chinese)
[11] Desbrieres J. Cement cake properties in static filtration. Influence of polymeric additives on cement filter cake permeability[J]. Cement & Concrete Research, 1993, 23(2):347-358
[12] 尤军. 触变性水泥浆体系与应用研究[D]. 山东青岛:中国石油大学,2010 You Jun. Research and application on thixotropic cement slurry[D]. Shandong Qingdao:China University of Petroleum, 2010(in Chinese)