基于Ansys Workbench的换热管断裂行为模拟分析

摘要

某石化企业焦油蒸馏装置的配套换热器在运行了3年之后,换热器内多根换热管发生了泄露和断裂。为了查明换热器换热管的失效原因,利用Ansys Workbench 13.0软件建立了流固耦合模型,通过流固耦合模拟获得了换热管束的真实应力状态。结果表明:热酚油进口附近的换热管承受了比较高的拉应力;同时研究了换热管内外流体对换热管的腐蚀作用,确定了冷却水中的氯离子和热焦油中的硫元素是造成换热管腐蚀的主要杂质。最终,根据换热管断口形态,确定了应力腐蚀开裂(SCC)是导致换热管失效的主要原因。

	Service

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	王晓静
	王磊
	郜维栋

关键词：换热器；换热管失效；应力腐蚀开裂； Ansys

Abstract：

A number of tube leaks and fractures occurred on a heat exchanger used in a tar distillation unit after operation of only three years. In order to identify the cause of this failure, a fluid-structure interaction simulation using Ansys Workbench 13.0 was performed to calculate its state of real stress distribution. The result revealed that the tubes which were close to the hot oil inlet suffered from high tensile stress. At the same time, chlorine and sulfur element which were in the cold water and hot oil respectively had corrosive effects to the tubes. Finally, the morphological feature of fracture was studied. It was found that tube failure was mainly caused by stress corrosion cracking (SCC).

Keywords： heat exchanger； tube failure； stress corrosion cracking； Ansys

Received 2013-08-16;

Corresponding Authors: 王磊, E-mail: xw0919@tju.edu.cn。 Email: xw0919@tju.edu.cn

About author: 王晓静(1963-),男,副教授,主要从事化工机械设备,干燥和造粒技术等的研究。

引用本文:

王晓静, 王磊, 郜维栋.基于Ansys Workbench的换热管断裂行为模拟分析[J]. 化学工业与工程, 2016,33(1): 90-95

Wang Xiaojing, Wang Lei, Gao Weidong.Failure Analysis of Heat Exchange Tubes Based on Ansys Workbench[J]. Chemcial Industry and Engineering, 2016,33(1): 90-95

[1] ASME. ASME Boiler & pressure vessel code[S]. 2010
[2] CSCBPV. GB 151-1999 Tubular heat exchangers[S]. 1999
[3] TEMA. Standard of tubular exchanger manufactures association[S]. 1999
[4] VDTUV. AD 2000 CODE technical rules for pressure vessels[S]. 2003
[5] Gao Z, Sun W, Jin W, et al. Study on tube pulling apart load in tubular heat exchangers with FEA method[C]. ASME, 2005
[6] 郭崇志, 周洁. 固定管板式换热器的温差热应力数值分析[J]. 化工机械,2009, 36(1): 41-46 Guo Chongzhi, Zhou Jie. Numerical analysis of the thermal stress induced by temperature differences of fixed tube-sheet heat exchangers[J]. Chemical Engineering & Machinery,2009, 36(1): 41-46 (in Chinese)
[7] 谢龙汉, 赵新宇, 张炯明. ANSYS CFX流体分析及仿真[M]. 北京:电子工业出版社, 2012 Xie Longhan, Zhao Xinyu, Zhang Jiongming. Ansys CFX fluid analysis and simulation[M]. Beijing: Publishing House of Electronics Industry, 2012 (in Chinese)
[8] 郭崇志, 肖乐. 换热器流固传热边界数值模拟温度场的顺序耦合方法[J]. 化工进展, 2010, 29(9): 1 615-1 619 Guo Chongzhi, Xiao Le. A sequence coupling method for numerical simulation of temperature field in liquid-solid heat transfer boundary of a heat exchanger[J]. Chemical Industry and Engineering Progress, 2010,29 (9):1 615-1 619 (in Chinese)
[9] Ansys Inc. Ansys Workbench Help Release 13.0[DB/OL]. 2010
[10] 钱世刚, 尤刚. 奥氏体不锈钢(1Cr18Ni9Ti)管材在含有氯离子介质中腐蚀的原因分析[J]. 贵州化工,2012, 37 (1): 25-29 Qian Shigang, You Gang. The analysis of corrosion cause of austenitic stainless steel (1Cr18Ni9Ti) tubular product in media containing chloride-ion[J]. Guizhou Chemical Industry,2012, 37 (1): 25-29 (in Chinese)
[11] 林海潮, 余家康, 史志明, 等. 含硫原油炼制过程中活性硫腐蚀[J]. 腐蚀科学与防护技术, 2000, 12(6): 341-345 Lin Haichao, Yu Jiakang, Shi Zhiming, et al. Corrosion by active sulfur species in petroleum refineries[J]. Corrosion Science and Protection Technology,2000, 12(6): 341-345 (in Chinese)
[12] 沈士明. 含缺陷承压设备安全分析技术[M]. 北京:中国石化出版社, 2011
[13] 王志文, 徐宏, 关凯书. 化工设备失效原理与案例分析[M]. 上海:华东理工大学出版社, 2010