MFI型分子筛膜的修复

摘要采用二次生长法制备完备的MFI型分子筛膜，在高温脱除模板剂后测试其CO₂/N₂分离性能，分离因子低，说明膜存在较大的缺陷。采用纳米SiO₂对分子筛膜进行修复，SiO₂修复后的分子筛膜对CO₂/N₂分离因子由1.6提高到5.0，且修复后的分子筛膜的性能很稳定。此外，该修复方法具有良好的重复性，用于多个具有低分离因子的膜都得到了比较好的效果

	Service

	把本文推荐给朋友 MFI分子筛膜\|缺陷修复\|纳米SiO₂\|分离 ”几篇好文章，特向您推荐。请点击下面的网址：" name=neirong>
	加入我的书架
	加入引用管理器
	Email Alert
	RSS
	作者相关文章
	杨军
	刘秀凤

关键词： MFI分子筛膜')" href="#">font-size: 9pt" lang="EN-US"> MFI分子筛膜缺陷修复纳米SiO₂ 分离

Abstract： Defect-Free MFI zeolite films on α-Al₂O₃ were fabricated by secondary growth method. The membrane generated large defect during calcination leading to low CO₂/N₂ separation selectivity. We used nanosized SiO₂ to heal the defect of original membrane. After healing process, the separation factor of CO₂/N₂ could be enhanced to ca.5.0 while it was about 1.6 for the original membrane. The membrane showed high stability after healing. In addition, the method is convenient and feasible to repair defects of membrane with high reproduction.

Keywords： MFI zeolite membrane defect healing nano-SiO₂ separation

Received 2012-11-28;

Fund:

多晶分子筛膜缺陷的选择性修复与过程机理研究（21076154）。

Corresponding Authors: 刘秀凤，电话：（022）27405165，E-mail:xfliu@tju.edu.cn。 Email: xfliu@tju.edu.cn

About author: 杨军（1987-），男，硕士研究生，研究方向：先进膜材料制备与应用。

引用本文:

杨军, 刘秀凤.MFI型分子筛膜的修复[J]. 化学工业与工程, 2013,30(6): 1-4

YANG Jun, LIU Xiu-Feng.Defect Healing of MFI Zeolite Membranes[J]. Chemcial Industry and Engineering, 2013,30(6): 1-4